Abstract:In this work, two kinds of YSZ nano powders were used as the raw materials to prepare thermal barrier coatings (TBC) via atmospheric plasma spraying. Firstly, raw materials with different original morphologies constitute feedstocks with varying internal structures. Secondly, these feedstocks, after spraying, form TBCs with different structures and porosity. Based on this, the differences in the morphologies of the raw materials may result in variations in the performance of the coatings. Therefore, the high-temperature performance of the corresponding TBCs was assessed comprehensively. Notably, the TBC prepared from flaky-YSZ (FYSZ) nano raw materials exhibited failure after only 84 thermal shock cycles, while the TBC prepared from granular-YSZ (GYSZ) nano raw materials maintained functionality even after 100 thermal shock cycles. Meanwhile, the GYSZ TBC demonstrates a better resistance to high-temperature oxidation with slower TGO growth. The failure mechanism of the TBCs was analyzed, focusing on the morphologies and structural characteristics. The findings highlight that disparities in raw materials' morphologies play a pivotal role in regulating the high-temperature service performance of the TBCs. The GYSZ raw materials are conducive to the formation of denser feedstocks, leading to decreased porosity in the coatings. In addition, their small size and uniform particle distribution facilitate the formation of columnar grains in the coating, enhancing the interlayer bonding strength of the GYSZ TBC. Consequently, during high-temperature service, the GYSZ TBC can effectively impede the growth of the thermally grown oxide (TGO) and alleviate the associated thermal mismatch stress, thereby ensuring a prolonged service life of the TBC. This work establishes a theoretical foundation for designing the performance of TBCs based on modulating the morphologies of raw materials.

Effect of Bionic Unit Shapes on Solid Particle Erosion Resistance of ZrO2–7wt%Y2O3 Thermal Barrier Coatings Processed by Laser

Effect of Bionic Unit Shapes on Solid Particle Erosion Resistance of ZrO 2 –7wt%Y 2 O 3 Thermal Barrier Coatings Processed by Laser

Effect of Bionic Unit Shapes on Solid Particle Erosion Resistance of ZrO–7wt%YO Thermal Barrier Coatings Processed by Laser

Preparation and Solid Particle Erosion Behaviors of Plasma-Sprayed and Laser-Remelted ZrO2-7wt.%Y2O3 Thermal Barrier Coatings

Thermal Shock Resistance of Thermal Barrier Coatings with Different Surface Shapes Modified by Laser Remelting

Wear Resistance of Different Bionic Structure Manufactured by Laser Cladding on Ti6Al4V

Effect of Bionic Units Fabricated by WC-NiCrBSiFe Laser Cladding on High-Temperature Erosion Wear Resistance of 304 Stainless Steel

Solid particle erosion behavior of thermal barrier coatings produced by atmospheric plasma spray technique

Effect of TiAl3 Content on Thermal Shock Resistance of Bionic Self-healing Thermal Barrier Coatings

Foreign Object Damage Behavior and Failure Mechanism of Al2O3-modified TBCs Prepared by PS-PVD

Microstructure and anti-ablation of laser cladding Ti-Zr-B-C coating on TC11 titanium alloy

Influence of interface morphology on erosion failure of thermal barrier coatings

Solid Particle Erosion Behavior of La2Ce2O7/YSZ Double-Ceramic-Layer and Traditional YSZ Thermal Barrier Coatings at High Temperature

Influence of Particle Shape on Erosion Behavior of EB-PVD Thermal Barrier Coatings

Laser-induced concave/convex micro-textures array for enhancing performance of surface coatings: Bond coating in thermal barrier coating system

Experimental Investigation and Theoretical Prediction on the Erosion Resistance of the Y0.5Gd0.5TaO4 Thermal Barrier Coatings at Room Temperature

High Performance Nanostructured ZrO2 Based Thermal Barrier Coatings Deposited by High Efficiency Supersonic Plasma Spraying

Preparing and Study of EB-PVD Thermal Barrier Coatings on Titanium Substrates

Effect of Morphology, Impact Velocity and Angle of the CaO-MgO-Al2O3-SiO2 (CMAS) Particle on the Erosion Behavior of Thermal Barrier Coatings (TBCs): A Finite Element Simulation Study

The Effect of Two Raw YSZ Materials with Different Morphology on TBCs Via Atmospheric Plasma Spraying: Microstructures and High-Temperature Performance

Multi-ceramic phases synergistically reinforced titanium matrix composite coating deposited by laser cladding: Effect of B 4 C content on the microstructure and wear properties