Preparation of spherical α‐Al 2 O 3 nanoparticles by microwave hydrothermal synthesis and addition of nano‐Al seeds
Zhiyuan Wang,Zenghui Mai,Yixiao Wu,Ying Wang,Zhenzhen Cao,Mingliang Li,Bingbing Fan,Gang Shao,Hailong Wang,Hongliang Xu,Rui Zhang,Hongxia Lu
DOI: https://doi.org/10.1111/jace.18524
IF: 4.186
2022-04-28
Journal of the American Ceramic Society
Abstract:Due to their special appearance, spherical α‐Al2O3 nanoparticles play an important role for obtaining high performance structural and functional ceramics. However, there are still problems such as easily agglomerates to form worm‐like structures at high temperatures and difficult availability of spherical nanoparticles. In this study, spherical α‐Al2O3 nanoparticles with high dispersion were prepared by combination of microwave hydrothermal method and addition of nano‐Al particles as seeds. Firstly, spherical amorphous alumina precursors were synthetized by microwave hydrothermal method at 100°C for 30 min using Al2(SO4)3∙18H2O, Al(NO3)3∙9H2O and urea as raw materials, and then, spherical α‐Al2O3 nanoparticles with diameter of about 66 nm were acquired after calcined the precursor at 1050°C for 90 min by adding nano‐Al seeds, which reduced the calcination temperature by 50°C and holding time by 30 min compared to that without seeds. Kinetic analysis shows that 5 wt.% nano‐Al seeds can reduce the activation energy of crystalline transition of γ‐Al2O3 to α‐Al2O3 from 516.51 kJ/mol to 474.37 kJ/mol. Moreover, the microscopic mechanism of nano‐Al particles as seeds was investigated. The characterizations of sintering properties show that spherical α‐Al2O3 nanoparticles facilitate the acquisition of uniform microstructure for resulting ceramic and the fracture modes include both intergranular and transgranular fracture.This article is protected by copyright. All rights reserved
materials science, ceramics