New Insights into the Influencing Mechanism of Ultrasonic Vibration on Interface of Al/Mg Bimetal Composites by Compound Casting Using Simulation Calculation and Experimental Verification

Qingqing Li,Wenming Jiang,Yuancai Xu,Linghui Yu,Xiaopeng Yu,Zitian Fan

DOI: https://doi.org/10.1016/j.compositesb.2024.111726

2024-01-01

Abstract:In this work, the numerical simulation of acoustic pressure distribution in ultrasonic vibration-assisted compound casting of Al/Mg bimetal composites was conducted. Relevant experimental verification was also performed to understand the influence of ultrasonic vibration treatment (UVT) on the interfacial microstructures and mechanical properties of the Al/Mg bimetal composites. Results revealed that the acoustic pressure distributions in the AZ91D melt were related to the vibration frequencies. The effective cavitation area at the Al/Mg interface reached the maximum percentage of 95.6 %, with the ultrasonic frequency of 20 kHz. The experimental results found that the Al/Mg interface without UVT was composed of Al -Mg intermetallic compounds (IMCs, i.e., Al 3 Mg 2 and Al 12 Mg 17 ) layer and eutectic layer. The oxide film and gas gap were existed between the two layers. The Mg 2 Si particles were gathered at the IMCs layer. The interfacial grains were coarse and their growth was directional. With UVT, the effective cavitation was occurred at the Al/Mg interface. The oxide film was broken, and the gas gap was eliminated. The interfacial microstructures were significantly refined. Due to the accelerated elemental diffusion and solute transfer by UVT, a more homogeneous Al/Mg interface was obtained. The Mg 2 Si particles were refined and formed at the eutectic layer. The microhardness mismatch of the IMCs layer and eutectic layer was decreased by UVT. The shear strength of the Al/Mg bimetal composites with UVT was enhanced to 62.2 MPa, which increased by 62.8 %, compared with that without UVT.