Comparative Investigation on the Fretting and Sliding Wear Properties of TC4 Against GCr15 under Different Temperatures

Dian Chen,Po Zhang,Qing Deng,Mengjie Deng,Zhiwen Yue,Zhaobing Cai,Le Gu
DOI: https://doi.org/10.1016/j.triboint.2024.109980
IF: 5.62
2024-01-01
Tribology International
Abstract:In industrial settings, the same friction pair can undergo both fretting and sliding wear depending on the working conditions. This study compares the fretting and sliding wear behaviors of TC4 against GCr15 at various temperatures. The results indicate that in fretting tests, the average friction coefficient decreases with increasing temperature, while in sliding tests, it shows the opposite trend. As the temperature rises, the material transfer is intensified, and a significant amount of Fe2O3 oxide friction layer forms on the surface of TC4 alloy, providing protection to the worn surface and decreasing the wear rate. At 300 degree celsius, adhesive wear in fretting wear is more severe than sliding wear, with peeling being more pronounced around the wear scar of sliding wear.
What problem does this paper attempt to address?