Improved Mechanical Properties of Al-xMg-yZn-Cu Alloys Via Optimized Mg/Zn Ratio and Thermomechanical Processing

Yu-Qiao Zhao,Hai-Long Jia,Teng Tian,Tao Gu,Pin-Kui Ma,Jia-Wang Song,Min Zha,Hui-Yuan Wang
DOI: https://doi.org/10.1016/j.msea.2024.146916
2024-01-01
Abstract:Three Al-xMg-yZn-1Cu alloys with equal total alloying element contents but different Mg/Zn ratios have been prepared in this work, i.e., Al-6Mg-1Zn-1Cu, Al-5Mg-2Zn-1Cu and Al-4Mg-3Zn-1Cu alloys. The influences of Mg/Zn ratios on microstructure and mechanical properties of heat-treated Al-xMg-yZn-1Cu alloys have been systematically studied. The results show that Al-xMg-yZn-1Cu alloys with higher Zn contents exhibit the faster aging response as Zn atom features the largest diffusion coefficient. Additionally, rod shaped and ellipsoidal T ' precipitates are observed in the Al-6Mg-1Zn-1Cu alloy. While in Al-4Mg-3Zn-1Cu alloy under TMT-2 process, T ' precipitates mainly exist in an ellipsoidal shape, with a higher number density (similar to 1.79 x 10(23) m-3) and smaller size (similar to 4.1 nm) compared to the Al-6Mg-1Zn-1Cu alloy. The optimized thermomechanical treatment (80 degrees C/5 h + rolling + 130 degrees C/x h) could effectively improve the yield strength of Al-5Mg-2Zn-1Cu and Al-4Mg-3Zn-1Cu alloys, with values increasing from similar to 419 MPa to similar to 441 MPa-similar to 454 MPa and similar to 470 MPa, respectively. In contrast, the Al-6Mg-1Zn-1Cu alloy exhibit almost no increment in yield strength after the same thermomechanical treatment. This could mainly be attributed to the higher density of T ' precipitates in alloys with higher Zn contents, resulting from the higher nucleation rate of T ' precipitates caused by high contents of Zn atoms featuring fast diffusion rates, with the assistance of dislocations introduced by rolling. This work provides theoretical supports for the development and production of age-hardenable Al-xMg-yZn-1Cu alloys.
What problem does this paper attempt to address?