Abstract:Although the precipitation and recrystallization of Mg-Al-Ca-Mn based alloys have been well investigated individually, there is still a lack of a detailed investigation on the effect of the Al-rich clusters, Mn-rich pre-cipitates and/or Ca-rich Laves phases formed from dynamic precipitation during rolling on the grain size and texture as well as yield strength. Here, we have investigated the effect of Mn (1 wt. %) on the dynamic pre-cipitation and yield strength of rolled Mg-3Al-1Ca alloy after rolling up to 1 and 6 passes (at 350 degrees C and 300 degrees C). It was found that an effective grain refinement can be obtained due to the fact that the dynamic precipitation enhances dynamic recrystallization by particle stimulated nucleation (PSN) mechanism. No significant texture change was obtained although the dynamic precipitation of Mn-rich particles due to the addition of 1 wt. % Mn results in a change from an RD-split texture to a strong basal texture. Three different Mn-rich phases ((i) large primary Al8Mn5 phase, (ii) the long plated-shaped Al8Mn5 phase, and (iii) nanoscale Al8Mn5 phase), C15 Laves phase (Al2Ca) and Al-rich clusters (G.P. zone), were observed, while no plate-shaped Al-Ca precipitate was observed on the basal plane of alpha-Mg matrix, indicating a competition among the formation of Al-rich clusters, plate-like Al-Ca precipitates, Ca-rich Laves phase, and Mn-rich phase within alpha-Mg matrix. Dispersion strengthening by the Ca-rich Laves phase, Mn-rich phase and Al-rich clusters is proposed to be attributed to the significant improvement of yield strength. This investigation highlights the importance of elucidating the effect of the dynamic precipitation on yield strength of rolled Mg-3Al-1Ca-1Mn alloys and provides helpful hints to further optimize the deformation and mechanical properties of Mg-Al-Ca-Mn based alloys.

Role of Ca Content on Microstructure, Mechanical Properties and Strain Evolution of As-Rolled Mg-Al-Ca-Zn-Mn Alloy

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Effects of Single-Pass Large-Strain Rolling on Microstructure and Mechanical Properties of Mg-Al-Ca Alloy Sheet

Comparative Study of the Microstructure Evolution and Mechanical Properties of Zn-0.1Mg-0.02Ca Alloy under Cold Rolling and ECAP

Effect of Ca/Al Ratio on Microstructure and Mechanical Properties of Mg-Al-Ca-Mn Alloys

Achieving High Strength in Micro-alloyed Mg-Al-Ca-Zn-Mn-Ce Alloy Sheet Processed by Single-Pass Large-Strain Rolling

Effect of Reduction in Thickness and Rolling Conditions on Mechanical Properties and Microstructure of Rolled Mg-8Al-1Zn-1Ca Alloy

Enhancing Mechanical Properties of Rolled Mg-Al-Ca-Mn Alloy Sheet by Zn Addition

Influence of Ca Content on Microstructure and Mechanical Properties of Extruded Mg–Al–Ca–Mn Alloys

The Role of Ca on the Microstructure and Tensile Properties of Mg-Al-Zn-Ca Alloys

Effect of Dual Deformation Processes on the Microstructure and Mechanical Properties of Low-Alloyed Mg-Zn-Ca-Mn Alloy

Microstructure Evolution and Mechanical Properties of High-Strength Mg-Gd-Y-Zn-Mn Alloy Processed by Asymmetric Hot Rolling

Effect of Rolling Reduction on the Microstructure and Mechanical Properties of Hot-Rolled Mg-Li-Al-Ca Alloys

Microstructure and Mechanical Properties of Extruded Mg–Zn–Mn–Ca Alloys

Dynamic recrystallization, texture and mechanical properties of high Mg content Al–Mg alloy deformed by high strain rate rolling

Microstructure and mechanical property of multi-pass low-strain rolled Mg-Al-Zn-Mn alloy sheet

Effect of Rolling Strain on Microstructure and Tensile Properties of Dual-Phase Mg–8Li–3Al–2Zn–0.5Y Alloy

Elucidating Dynamic Precipitation and Yield Strength of Rolled Mg–Al–Ca–Mn Alloy

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys

Effects of Ca addition on the microstructure and mechanical properties of Mg–Zn–Sn–Mn alloys

Enhanced Performance of Mg–Zn–Y–Mn Alloy Via Minor Ca Addition