Abstract:A highly efficient catalyst of a CoaMnbOx mixed oxide prepared by the co-precipitation method was developed for the selective catalytic reduction (SCR) of NOx with ammonia. With an increase in the Mn content, the catalytic activity of the CoaMnbOx mixed oxide exhibited a volcano-type tendency, and when Co/Mn molar ratio reached 7:3 (Co7Mn3Ox), the operation temperature for achieving > 80% NOx conversion was 170 degrees C (116-285 degrees C window). The formation of spinel structured MnCo2O4 is highly important, and the presence of the spinel structure in Co7Mn3Ox contributes to the increase in active sites and thermal stability and promotes SO2 and/or H2O resistance. In comparison with MnOx or CoOx alone, the CoaMnbOx catalysts possess improved redox properties and more surface acid sites due to synergistic effects between the Co and Mn species. Among the CoaMnbOx catalysts with different Co/Mn molar ratios, a higher NH3 and NO + O-2 adsorption ability was found for the Co7Mn3Ox catalyst, originating from its MnCo2O4.5 phase and higher surface area, which leads to the higher activity of the Co7Mn3Ox, catalyst. In situ DRIFTs indicated that bridging nitrate and bidentate nitrate are the intermediate species in the NH3-SCR reaction, and the high NO adsorption ability and improved redox properties of the Co7Mn3Ox catalyst are beneficial for the formation of nitrate species on the catalyst surface. Furthermore, NH3 species adsorbed at Lewis acid sites taken part in SCR reaction, while the reactivity of NH3 species adsorbed at Bronsted acid was not definitized.

IrSn Bimetallic Clusters Confined in MFI Zeolites for CO Selective Catalytic Reduction of NOx in the Presence of Excess O2.

IrSn Bimetallic Clusters Confined in MFI Zeolites for CO Selective Catalytic Reduction of NO x in the Presence of Excess O 2

Tailoring Iridium Valence States on ZSM-5 for Enhanced Catalytic Performance in CO Selective Catalytic Reduction of NO under Oxygen-Enriched Environments

Self-Confinement Created for a Uniform Ir–Ni/SiO2 Catalyst with Enhanced Performances on CO2 Reforming of Methane

Isolating Contiguous Ir Atoms and Forming Ir–W Intermetallics with Negatively Charged Ir for Efficient NO Reduction by CO

Insight into the Mechanism of Selective Catalytic Reduction of NO by CO over a Bimetallic IrRu/ZSM-5 Catalyst in the Absence/Presence of O2 by Isotopic C13O Tracing Methods

Single Ir Atoms Anchored on Ordered Mesoporous WO 3 Are Highly Efficient for the Selective Catalytic Reduction of NO with CO under Oxygen‐rich Conditions

Novel shielding and synergy effects of Mn-Ce oxides confined in mesoporous zeolite for low temperature selective catalytic reduction of NOx with enhanced SO2/H2O tolerance

Strong metal oxide-zeolite interactions during selective catalytic reduction of nitrogen oxides

Unraveling the Synergistic Mechanism of Ir Species with Various Electron Densities over an Ir/ZSM-5 Catalyst Enables High-Efficiency NO Reduction by CO

Co Single Atoms and CoOx Nanoclusters Anchored on Ce0.75Zr0.25O2 Synergistically Boosts the NO Reduction by CO

Sn-MFI as active, sulphur and water tolerant catalysts for selective reduction of NOx

Synthesis of Bimetallic MOFs MIL-100(Fe-Mn) As an Efficient Catalyst for Selective Catalytic Reduction of NO X with NH 3

Subnanometric Pt on Cu Nanoparticles Confined in Y‐zeolite: Highly‐efficient Catalysts for Selective Catalytic Reduction of NO x by CO

MnyCo3−yOx Bimetallic Oxide Prepared by Ultrasonic Technology for Significantly Improved Catalytic Performance in the Reduction of NOx with NH3

High Performance Iridium Loaded on Natural Halloysite Nanotubes for CO-SCR Reaction

Highly dispersed MnOx-FeO(x)supported by silicalite-1 for the selective catalytic reduction of NO(x)with NH(3)at low temperatures

NiyCo1-yMn2Ox Microspheres for the Selective Catalytic Reduction of NOx with NH3: the Synergetic Effects Between Ni and Co for Improving Low-Temperature Catalytic Performance

Spinel Structured CoaMnbOx Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3

Activity Test and Mechanism Study of 3DOM Ce 0.8 M 0.1 Zr 0.1 O 2 (M=Cr, Sn, Fe, Co, Ni, Mn, Cu) Catalyst in the Selective Catalytic Reduction of NO by CO**

Coll 279-A Novel Indium On Tungstated Zirconia Catalyst For Selective Catalytic Reduction Of Nox With Methane In The Presence Of Oxygen