Abstract:Carbon fibre reinforced silicon carbide (C/C-SiC) composite materials have attracted increasing attention in brake system of high-speed trains, due to their low density, high specific strength, thermal stability, and frictional wear performance. This study aims to explore the mechanical properties of the 2.5D C/C-SiC composites, in order to characterise its potential application to the friction braking system of high-speed trains. To comprehensively evaluate the mechanical performance of the 2.5D C/C-SiC composites, the chemical vapor infiltration (CVI) method was adopted to prepare novel samples with high densification and low content of residual Si. The mechanical properties and failure mechanisms of the composites were investigated under various loading conditions, including tension, compression, bending, and shear tests. The experimental results indicated that the 2.5D C/C-SiC composites exhibited superior mechanical properties, with average in-plane tensile strength, compressive strength, bending strength, and interlaminar shear strength reaching 127.67 MPa, 326.92 MPa, 355.74 MPa, and 9.77 MPa, respectively, which are 2-8 times higher than the mechanical properties of C/C-SiC composites in existing publications. Under different loading conditions, the composites demonstrated characteristics of ductile fracture, pseudo-plastic compression fracture, pseudo-plastic bending fracture, and brittle shear fracture. Both high fibre content and the formation of SiC structure were advantageous for enhancing the load-bearing performance of C/C-SiC composites. The outstanding mechanical properties of the 2.5D C/C-SiC composite render the brake disc highly resistant to deformation and cracking under high stress, thereby enhancing its durability and establishing it as the ideal material for the next generation of high-speed train brake discs.

Mechanical and Microstructure Characterisation of 2.5D C/C-SiC Composites Applied for the Brake Disc of High-Speed Train

Preparation and Dynamometer Tests of 3D Needle‐Punched C/C‐SiC Composites for High‐Speed and Heavy‐Duty Brake Systems

The Microstructure and Tribological Properties of Carbon Fibre Reinforced Carbon/SiC Dual Matrix Composites

Preparation and Properties of C/C-SiC Brake Composites Fabricated by Warm Compacted-in Situ Reaction

Coupled thermal-structural analysis of an axle mounted C/C-SiC brake disc for high-speed trains

Preparation of C/C–SiC Composite by Low Temperature Compression Molding–liquid Silicon Infiltration and Its Application in Automobile Brake

Manufacture and Properties of Carbon Fibre-Reinforced C/SiC Dual Matrix Composites

Tribological Properties and Thermal-Stress Analysis of C/C-SiC Composites During Braking

Microstructure and tribological properties of 3D needle-punched C/C–SiC brake composites

Microstructure and Properties of 3d Needle-Punched Carbon/Silicon Carbide Brake Materials

Preparation and Tribological Properties of C Fibre Reinforced C/Sic Dual Matrix Composites Fabrication by Liquid Silicon Infiltration

The Analysis of Friction and Wear Performance of C/C-SiC Composites

Oxidation Behaviour of C/C–SiC Brake Discs Tested on Full-Scale Bench Rig

Microstructure and mechanical properties of 3D needled carbon fibre reinforced carbon and silicon carbide composites

Three-dimensional needled carbon/silicon carbide composites with high friction performance

Frictional Properties of C/SiC Brake Materials

Manufacture and Tribological Properties of C/C-Sic Brake Composites Fabricated by Warm Compacted In-Situ Reaction

Research Progress of Carbon/Silicon Carbide Brake Materials

Braking Behavior of C/Sic Composites Prepared by Chemical Vapor Infiltration

Tribological Behavior and Mechanism of Carbon Fibre Reinforced Carbon and SiC Dual- Matrice Composites

C/C-SiC Composites for Advanced Friction Systems