Enhanced $j_{c}$ in $\hbox{\rm YBa}_{2}\hbox{\rm Cu}_{3}\hbox{O}_{7 - \delta}$ Thin Films by Low-Level Cr Doping

H. Jian,Z. Hui,Zhaorong Yang,Xuebin Zhu,Yuping Sun

DOI: https://doi.org/10.1109/tasc.2013.2270556

IF: 1.9489

2013-01-01

IEEE Transactions on Applied Superconductivity

Abstract:$\hbox{YBa}_{2}(\hbox{Cu}_{1 - {\rm x}}\hbox{Cr}_{\rm x})_{3}\hbox{O}_{7 - \delta}$ (${\rm x} = 0$, 0.02%, 0.04%, 0.06%) thin films were prepared by trifluoroacetate metal organic deposition on $ \hbox{LaAlO}_{3}$ (001) single crystal substrates. Critical current density and irreversibility field were correspondingly improved distinctly by Cr doping. Analysis suggested that the pinning type was $\delta l$ pinning for all derived thin films, and the dominant pinning type was not shifted to $\delta T_{c}$ pinning by Cr doping. Combined with the result that the critical superconducting temperature was not depressed by Cr doping, it was concluded that Cr probably occupied into the Cu(1) sites.