Abstract:Hydrogen enrichment induced by pipeline welding residual stress is a key issue affecting the safe service of hydrogen pipelines. In order to explore the influence of welding residual stress on hydrogen diffusion and the effect of heat treatment, an X80 pipeline model with a six-layer girth weld was established using ABAQUS software, and coupling analysis of temperature field, stress field, and hydrogen diffusion was carried out. The distribution of residual stress in the welding area and local inclusion area was analyzed, the relationship between the hydrostatic stress and hydrogen diffusion of the pipeline, and the influence of the direction and shape of the inclusion on hydrogen diffusion were explored, and the effect of post-weld heat treatment on the residual stress and hydrogen diffusion in the welding area and local inclusion area was studied. The hydrostatic stress curve is similar to the hydrogen concentration distribution curve, and hydrostatic stress can be considered the main driving force for hydrogen diffusion in the pipeline. As the angle between the inclusions and the hydrogen diffusion direction increases, the hydrogen diffusion flux will gradually decrease. The more slender the inclusions, the stronger the diffusion ability of parallel or 45° inclusions, and the weaker the diffusion ability of perpendicular inclusions. Hydrogen enrichment occurs in inclusions or inclusion boundaries before and after post-weld heat treatment of the pipeline, and the internal hydrogen concentration of hard inclusions is higher than that of soft inclusions. Post-weld heat treatment can significantly reduce welding residual stress and hydrostatic stress, thereby reducing hydrogen enrichment concentration.

Hydrogen Permeation Behavior at Different Positions in the Normal Direction of X42 and X52 Pipeline Steels

Experimental study on the temperature dependence of gaseous hydrogen permeation and hydrogen embrittlement susceptibility of X52 pipeline steel

Different aspects of hydrogen diffusion behavior in pipeline steel

Effect of Microstructure on Hydrogen-induced Cracking Propagation and Hydrogen Trapping Efficiency of Pipeline Steel

Effect of Hydrostatic Pressure on Hydrogen behavior on the surface of X70 pipeline steel

Synergic Effects of Temperature and Pressure on the Hydrogen Diffusion and Dissolution Behaviour of X80 Pipeline Steel

Experimental investigation on the hydrogen embrittlement characteristics and mechanism of natural gas-hydrogen transportation pipeline steels

Investigating variations in hydrogen-assisted crack propagation of X52 pipeline steel with different microstructural characteristics

Study on hydrogen resistance of x42 pipeline steel under electrochemical hydrogen charging condition

Effect of Cold Deformation on the Hydrogen Permeation Behavior of X65 Pipeline Steel

Safe pipelines for hydrogen transport

Hydrogen effect on a low carbon ferritic-bainitic pipeline steel

Investigation of hydrogen embrittlement behavior in X65 pipeline steel under different hydrogen charging conditions

Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures

Quantitative Study on Hydrogen Concentration–Hydrogen Embrittlement Sensitivity of X80 Pipeline Steel Based on Hydrogen Permeation Kinetics

Hydrogen effects on X80 pipeline steel in high-pressure natural gas/hydrogen mixtures

Effect of interaction between corrosion film and H2S/CO2 partial pressure ratio on the hydrogen permeation in X80 pipeline steel

Research on residual stress and hydrogen diffusion of X80 pipeline welded joint

Hydrogen diffusion simulation of the X80 pipeline steel girth weld zone considering the synergistic effect of the structure–stress–concentration field

Experimental comparison of gaseous and electrochemical hydrogen charging in X65 pipeline steel using the permeation technique

Influence of hydrogen volume/specimen surface area ratio on hydrogen embrittlement sensitivity of X52 pipeline steel