Study on Compatibility Assessment of Urban Natural Gas Pipeline Welded Joints under Hydrogen Environment
Songrui Guo,Xiang He,Lingxiao Shao,Xi Shen,Zhengli Hua
DOI: https://doi.org/10.1115/pvp2024-122760
2024-01-01
Abstract:Abstract Hydrogen, as one of the crucial carriers in achieving the green and low-carbon transition, plays a significant role in a multi-energy structure. Among the existing hydrogen transportation methods, the transportation of hydrogen in the form of hydrogen-blended natural gas through the existing urban natural gas pipeline network is an effective way to enhance transportation efficiency and substantially reduce costs. However, when hydrogen comes into contact with the metal materials of natural gas pipelines, it can lead to hydrogen embrittlement, resulting in a deterioration of the mechanical properties of the metal materials and even causing significant accidents. Notably, the welded joint area of gas pipelines is widely recognized as the vulnerable link in pipeline transportation systems because the microstructure and mechanical properties of the welded joint area differ significantly from those of the pipeline steel base material, making it the most susceptible site for hydrogen embrittlement-induced failure. In this study, using 20# steel as the research subject, specimens were taken from the vertical weld seam in its welded joint area. The slow strain rate tensile test, low cycle fatigue test and fatigue crack growth test under hydrogen environment were carried out to explore the variation of mechanical properties under different working conditions. The results demonstrate that with an increase in hydrogen content, the yield strength and tensile strength of the welded joint in 20# steel decrease slightly, resulting in a deterioration of mechanical properties. The elongation and reduction of area after fracture decrease, indicating reduced material plasticity and an intensified degree of hydrogen embrittlement. With the addition of hydrogen, the overall low cycle fatigue life of specimens decreases. The relative fatigue life for the three materials are 74.22%, 62.02%, and 46.05%, demonstrating a noticeable decline in fatigue performance. Hydrogen significantly increases the fatigue crack growth rate in the weld zone of 20# steel. At a hydrogen addition of 10vol%, the fatigue crack growth rate is already approximately 12 times higher than that in the reference environment with 0vol% hydrogen. Simultaneously, with the increase of hydrogen content, the fatigue crack growth rate and the degree of deterioration both escalate, and the deterioration indexes are all above 90 %. The research findings can be utilized to assess the compatibility of gas pipeline welded joints in a hydrogen environment.