Abstract:Abstract Hydrogen, as one of the crucial carriers in achieving the green and low-carbon transition, plays a significant role in a multi-energy structure. Among the existing hydrogen transportation methods, the transportation of hydrogen in the form of hydrogen-blended natural gas through the existing urban natural gas pipeline network is an effective way to enhance transportation efficiency and substantially reduce costs. However, when hydrogen comes into contact with the metal materials of natural gas pipelines, it can lead to hydrogen embrittlement, resulting in a deterioration of the mechanical properties of the metal materials and even causing significant accidents. Notably, the welded joint area of gas pipelines is widely recognized as the vulnerable link in pipeline transportation systems because the microstructure and mechanical properties of the welded joint area differ significantly from those of the pipeline steel base material, making it the most susceptible site for hydrogen embrittlement-induced failure. In this study, using 20# steel as the research subject, specimens were taken from the vertical weld seam in its welded joint area. The slow strain rate tensile test, low cycle fatigue test and fatigue crack growth test under hydrogen environment were carried out to explore the variation of mechanical properties under different working conditions. The results demonstrate that with an increase in hydrogen content, the yield strength and tensile strength of the welded joint in 20# steel decrease slightly, resulting in a deterioration of mechanical properties. The elongation and reduction of area after fracture decrease, indicating reduced material plasticity and an intensified degree of hydrogen embrittlement. With the addition of hydrogen, the overall low cycle fatigue life of specimens decreases. The relative fatigue life for the three materials are 74.22%, 62.02%, and 46.05%, demonstrating a noticeable decline in fatigue performance. Hydrogen significantly increases the fatigue crack growth rate in the weld zone of 20# steel. At a hydrogen addition of 10vol%, the fatigue crack growth rate is already approximately 12 times higher than that in the reference environment with 0vol% hydrogen. Simultaneously, with the increase of hydrogen content, the fatigue crack growth rate and the degree of deterioration both escalate, and the deterioration indexes are all above 90 %. The research findings can be utilized to assess the compatibility of gas pipeline welded joints in a hydrogen environment.

Hydrogen in pipeline steels: Recent advances in characterization and embrittlement mitigation

A review of hydrogen embrittlement in gas transmission pipeline steels

Advances in reducing hydrogen effect of pipeline steels on hydrogen-blended natural gas transportation: A systematic review of mitigation strategies

The Impact of Impurity Gases on the Hydrogen Embrittlement Behavior of Pipeline Steel in High-Pressure H2 Environments

Hydrogen blending in existing natural gas transmission pipelines: a review of hydrogen embrittlement, governing codes, and life prediction methods

A critical perspective on pipeline processing and failure risks in hydrogen service conditions

Use of existing steel pipeline infrastructure for gaseous hydrogen storage and transport: A review of factors affecting hydrogen induced degradation

Evaluating hydrogen embrittlement susceptibility of operated natural gas pipeline steel intended for hydrogen service

Hydrogen-induced degradation of high-strength steel pipeline welds: A critical review

Hydrogen embrittlement in hydrogen-blended natural gas transportation systems: A review

Inhibiting effect of carbon monoxide on gaseous hydrogen embrittlement of pipelines transporting hydrogen

Study on Compatibility Assessment of Urban Natural Gas Pipeline Welded Joints under Hydrogen Environment

Hydrogen related degradation in pipeline steel: A review

Study on hydrogen embrittlement susceptibility of X80 steel through in-situ gaseous hydrogen permeation and slow strain rate tensile tests

Hydrogen effects on X80 pipeline steel in high-pressure natural gas/hydrogen mixtures

Experimental study on the temperature dependence of gaseous hydrogen permeation and hydrogen embrittlement susceptibility of X52 pipeline steel

Embrittlement, degradation, and loss prevention of hydrogen pipelines

Effect of stress triaxiality on the hydrogen embrittlement micromechanisms in a pipeline steel evaluated by fractographic analysis

Safe pipelines for hydrogen transport

Research Progress and Prospects on Hydrogen Damage in Welds of Hydrogen-Blended Natural Gas Pipelines

Hydrogen Economy vs. Hydrogen Embrittlement: Indirect Electrochemical Determination of Hydrogen Diffusion in Steel