Abstract:Permanently implanted biomaterials may cause problems to the host body associated with long term chronic inflammation which would eventually require revision surgery. The development of biodegradable materials which can be absorbed, consumed and excreted by the patient is therefore of interest. Magnesium alloys have for a long time been considered as potential biomaterials for load-bearing applications due to their excellent biological properties including superior biochemical and biomechanical compatibility compared to other alternatives such as biodegradable polymers and bioceramics. However, the application of magnesium material in the biological area is still limited due to its intrinsically poor corrosion performance in the biological environments. Therefore, various methods have been explored to control the degradation rate of magnesium in biological fluid, of which plasma electrolytic oxidation (PEO) is the most promising method. PEO is a plasma-assisted anodising process that can convert the surface of magnesium into a ceramic layer, thus preventing the corrosive medium contacting the substrate; therefore, the degradation rate can be reduced. Furthermore, highly biocompatible coatings can be produced when appropriate electrolytes are used in the PEO process. Motivated by the beneficial properties of magnesium and corrosion protection provided by the PEO technique, considerable efforts have been devoted towards the development of magnesium implants based on PEO protection. Nevertheless, the corrosion rate of magnesium has not been reduced to an acceptable level and a universal PEO process appropriate for magnesium has not yet been established. In the present study, PEO processes on commercially pure (cp) magnesium and the resulting coating characteristics have been systematically studied. Through this progressive study, a biologically friendly electrolyte containing Ca and P compounds have been developed. An appropriate current regime for this electrolyte has also been studied. Finally, a hydroxyapatite layer, intended to enhance the sample bioactivity, was deposited on the PEO coated cp magnesium. The PEO process was studied according to key electrical characteristics including voltage transient, and voltage/current waveforms. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD) were employed to study the surface and cross-sectional morphology, elemental composition, phase composition of the coatings. Residual stress induced by the PEO process is also studied using XRD method. The corrosion properties of the coated samples in simulated body fluid (SBF) were studied using electrochemical methods including open circuit potential (OCP) monitoring, electrochemical impedance spectroscopy (EIS) measurement, and potentiodynamic polarisation scans. The mechanical properties, including static tensile properties and cyclic fatigue performance of the coated samples were also studied to verify the applicability of magnesium in biological areas from the mechanical point of view. The results indicated that the combination of a pulsed unipolar (PUP) current regime of 3000 Hz and an electrolyte composed of 12 g/l Na3PO4•12H2O and 2g/l Ca(OH)2 provides the best process stability and success of Ca and P incorporation. Moreover, the corrosion resistance of cp magnesium in the SBF could be improved by more than 10 times. Nevertheless, such protection is very limited as the coating was degraded rapidly in the simulated body fluid, which is due to the chemical instability of MgO at the pH of SBF. Tensile and cyclic fatigue tests demonstrated that the PEO coated cp magnesium possesses sufficient mechanical properties for general load-bearing biomedical applications even though the fatigue strength is significantly deteriorated by the surface modification. Further work required to achieve better control over the biodegradation process of Mg implants can be outlined as follows: (i) robustness of the developed PEO process should be explored on other corrosion resistant magnesium alloys containing biologically friendly elements (like Ca, Zn, Mn); (ii) addition of F-, SiO32- in the electrolyte to facilitate the formation of stable compounds besides MgO in the PEO coating, thus reducing the degradation rate of magnesium based implants

Long-Term Degradation Performance and Biocompatibility of Plasma Electrolytic Oxidation Coated Mg-0.45ca-Xzn Alloys Prepared Using a Fluoride-Based Electrolyte

In Vitro Degradation and Corrosion Evaluations of Plasma Electrolytic Oxidized Mg-Zn-Ca-Si Alloys for Biomedical Applications

Improved Blood Compatibility and Cyto-Compatibility of Zn-1Mg Via Plasma Electrolytic Oxidation

Enhancing the corrosion resistance of a novel bio-compatible Mg-1Zn-0.45Ca alloy in simulated body fluid by a phosphate treated PEO coating

In Vitro Degradation and Electrochemical Corrosion Evaluations of Microarc Oxidized Pure Mg, Mg-Ca and Mg-Ca-Zn Alloys for Biomedical Applications

A Plasma Electrolytic Oxidation Coating on High-Purity Mg with Excellent Long-Term Degradation Performance and Biocompatibility

Degradation Rate Control Issues of PEO-Coated Wrought Mg0.5Zn0.2Ca Alloy

Advances in amelioration of plasma electrolytic oxidation coatings on biodegradable magnesium and alloys

Controllable Degradable Plasma Electrolytic Oxidation Coated Mg Alloy for Biomedical Application

Bioactivity Performance of Pure Mg after Plasma Electrolytic Oxidation in Silicate-Based Solutions

Degradation behavior, biocompatibility and antibacterial activity of plasma electrolytic oxidation treated zinc substrates

Preparation and Characterization of A Calcium-Phosphate-Silicon Coating on A Mg-Zn-Ca Alloy Via Two-Step Micro-Arc Oxidation

Investigating the mechanical properties and corrosion resistance of extruded Mg-1Zn-xCaO (x=0, 0.5, 1.0 wt%) materials

Corrosion Resistance and Biodegradability of Micro-Arc Oxidation Coatings with the Variable Sodium Fluoride Concentration on ZM21 Magnesium Alloys

Microstructure and Corrosion Behavior of Ca/P Coatings Prepared on Magnesium by Plasma Electrolytic Oxidation

Incorporation of Magnesium Phosphate into Magnesium Oxide on MgAg Alloy Through Plasma Electrolytic Oxidation

Enhanced Corrosion Resistance in High-Strength Biodegradable Mg-Zn-Ca-Si Glassy Alloy Composite via Preparation of a Self-Sealing Plasma Electrolytic Oxidation Layer

Effects of ZnO nanoparticles addition to plasma electrolytic oxidation coatings on magnesium alloy: Microstructure, in vitro corrosion and antibacterial properties

Investigation of Plasma Electrolytic Oxidation of Commercially Pure Magnesium for Biomedical Applications

Effect of CaO Additive on the Properties of Plasma Electrolytic Oxidation Coatings on AZ31 Mg Alloy

Preparation and Degradation Behavior of Composite Bio-Coating on ZK60 Magnesium Alloy Using Combined Micro-Arc Oxidation and Electrophoresis Deposition