Abstract:The corrosion of steel structures in aggressive marine environments is a vital issue that induces significant degradation of their performance and lifespan. Herein, three arc-sprayed ZnAl coatings with varied Al contents of 0 wt.%, 15 wt.%, and 50 wt.% were deposited onto a hull steel substrate. The effect of Al content on the long-term corrosion protection performance of ZnAl coatings left in a chloride-containing solution for 840 h was systematically investigated. The evolutions of open-circuit potential, polarization curves, and electrochemical impedance spectroscopy of different ZnAl coatings during the long-term immersion test were examined. The morphologies and phase constitutions of the corrosion products were characterized. The results indicated that the corrosion rate of ZnAl coatings decreased as the Al content increased, and the ZnAl50 coating exhibited the most superior long-term corrosion protection performance. Moreover, for the three ZnAl coatings with an Al contents varying from 0 to 50%, their corrosion rate increased with immersion time in the initial 360 h due to the formation of the unstable and porous corrosion product ZnO; after 360 h immersion, their corrosion rate decreased with the prolonging of immersion time. This was revealed to be related to the formation of different corrosion products. ZnO and stable Al2O3 were the main corrosion products for the pure Zn coating and ZnAl15 coating, respectively. Al2O3 and powerful layered double hydroxide Zn6Al2(OH)16CO3·4H2O were found to be the dominant corrosion products of the ZnAl50 coating, which was responsible for its remarkable long-term corrosion protection performance.

Comparative Study on the Corrosion Behavior of Two Arc Spraying Coatings in Simulated Marine Environments

Corrosion Mechanism of Arc Spraying Aluminum Coatings in Marine Environment

Effect of Al Content on the Long-Term Corrosion Behavior of Arc-Sprayed ZnAl Alloy Coatings

Corrosion Behavior of Aluminum Coating by Arc Spraying in Simulated Marine Splash Zone

Corrosion Resistance of Arc-Sprayed Aluminum Coating on Aluminum Alloy

Corrosion behaviors of arc-sprayed Al/Zn pseudo alloy coating on deep-water drilling riser's surface

Influence of Al contents on the long-term corrosion behaviors of cold-sprayed Zn-xAl coatings

Preparation, Wear Resistance, and Corrosion Performance of Arc-Sprayed Zn, Al, and Zn-Al Coatings on Carbon Steel Substrates

Corrosion Behaviour of Arc Sprayed Zn55Al Coatings on Q235 Steel in 3.5 wt% NaCl Solution

Corrosion Behaviour of Three Kinds of Arc Sprayed Coatings in Soil

Corrosion Behavior of High-Strength Pipeline Steel and Coatings in the Simulated Sea Water Environment

Corrosion Behavior of High-Pressure Cold-Sprayed Zn30Al Alloy Coating on Q235 Steel

Corrosion Behavior of Arc-Sprayed Pore-Sealed Zn and Al Coatings in Seawater Containing Sulfate-Reducing Bacteria (SRB)

Corrosion behavior and mechanism of electric arc-sprayed Al-Mg coating and Zn-Al-Mg pseudo-alloy coatings

Corrosion resistance of three arc-sprayed Zinc coatings in 3.5% NaCl solution

Degradation Behavior of Arc-Sprayed Zinc Aluminum Alloy Coatings for the Vessel Yongle in the South China Sea

Corrosion Behavior of Hot-Dip 55%Al-Zn Alloy Coated Sheet Steel Exposed to Different Seawater Zones in Qingdao

Corrosion Resistance of Al-based Coating Prepared by Arc Spraying

Corrosion Behaviour of Hot Dip Zinc and Zinc-Aluminium Coatings on Steel in Seawater

Corrosion Behaviors of Microarc Oxidation Coating and Anodic Oxidation on 5083 Aluminum Alloy

MICROSTRUCTURES AND SALT SPRAY CORROSION BEHAVIORS OF COLD SPRAYED Al COATINGS ON S355 STEEL IN MARINE ENVIRONMENT