Abstract:Lithium-ion batteries (LIBs) are widely used in modern society. Since LIBs represent a substantial fraction and sometimes even majority of the device cost, extending the lifetime of LIBs and understanding their degradation mechanisms draw an increasing attention. Graphite, commonly used as the negative electrode in LIBs, suffers from two main degradation mechanisms: loss of active material and loss of lithium-ion inventory. Formation of the so-called solid electrolyte interphase (SEI) layer is known as the key factor for functioning of the anode. On the one hand, its growth covering the electrode surface slows down Li-ion intercalation. On the other hand, the SEI layer both protects the graphite particles from exfoliation upon intercalation and the electrolyte from decomposition by preventing organic molecules from entering graphite. Due to surface defects of the graphite particles used in common LIBs, it is challenging to observe the SEI layer formation. Therefore, highly oriented pyrolytic graphite (HOPG), which has a perfectly smooth surface, is commonly used in SEI formation experiments. In this work, we have applied electrochemical analysis, as well as morphology and structure characterization to investigate processes involved into the formation of SEI layer. A three-electrode electrochemical cell setup was installed in a glove box under inert argon atmosphere. HOPG was used as the working electrode and lithium metal was employed as both the reference electrode (RE) and counter electrode (CE). The electrolyte was composed of 1M lithium hexafluorophosphate (LiPF 6 ) dissolved in 1:1 v/v mixture of ethylene carbonate (EC) and diethyl carbonate (DEC). Cyclic voltammetry (CV) was performed in voltage ranges of 2, 1.5, and 0.5 V versus Li/Li + . canning Electron Microscopy (Zeiss XB1540) and Atomic Force Microscopy (Ntegra Aura) were used to characterize the morphology and topography of the HOPG electrode after CV. X-ray Photoelectron Spectroscopy (XPS, Phoibos 150 1D-DLD, XR 50, Specs) was employed to measure the elemental composition and structure at the HOPG surface. When the cycling was performed between 3 – 2 V, small particles were observed on the surface of the HOPG, which can be assigned to the deposition of electrolyte. Homogeneous microspheres started to appear when the voltage reached below 1.5 V, which can be attributed to the formation of SEI particles. As the CV range increased, which also meant an increase in the depth of discharge (DOD), the density of microspheres on the surface increased as well. The diameter of the microspheres was found to be around 80 – 100 nm at a low lithiation level, and as the HOPG electrode became fully lithiated, the size of the particles slightly increased. This finding was supported by XPS measurements where the integral of the Li x PF y and Li x PF y O y peak, which is related to the main constituents of SEI layer, was found to be the largest (57.68% of the full F 1s spectra peak area) in the 3 – 0 V cycle range, while a lower peak (54.56%) was observed in the 3 – 0.5 V range (in the attached Figure). These results provide an indication of how the charging method affects the capacity fade and lifetime of the LIBs. The stage from 0.5 to 0 V on HOPG is approximately equivalent to 80-100% SOC for a full cell. As was found, in this stage, the SEI film grows thicker, thereby aggravating the aging of the cell. The lifetime of LIBs can therefore be extended if cycling at high SOC is avoided. Based on this, our future work will focus on the development of an optimized multi-step fast-charging method, which can reduce degradation and extend the lifetime of commercial lithium-ion batteries. Figure 1

Catalytic Decomposition of Ethylene Carbonate by Pyrrolic-N to Stabilize Solid Electrolyte Interphase on Graphite Anode under Extreme Conditions

Ultrafast Charge and Long Life of High-Voltage Cathodes for Dual-Ion Batteries Via a Bifunctional Interphase Nanolayer on Graphite Particles.

Correlating Graphite Surface with Interphase for Fast‐Charging and Low‐Temperature Operation

Reversible Cycling of Graphite Electrodes in Propylene Carbonate Electrolytes Enabled by Ethyl Isothiocyanate

Eliminating Graphite Exfoliation with an Artificial Solid Electrolyte Interphase for Stable Lithium‐Ion Batteries

Bifunctional Interphase Promotes Li+ De‐Solvation and Transportation Enabling Fast‐Charging Graphite Anode at Low Temperature

Artificially regulated interphase on natural graphite realizes rapid charge and durable high-temperature cycling of Li-ion batteries

Catalytic Strategies Enabled Rapid Formation of Homogeneous and Mechanically Robust Inorganic‐Rich Cathode Electrolyte Interface for High‐Rate and High‐Stability Lithium‐Ion Batteries

Engineering an Insoluble Cathode Electrolyte Interphase Enabling High Performance NCM811//Graphite Pouch Cell at 60 °C

Stable cycling and low-temperature operation utilizing amorphous carbon-coated graphite anodes for lithium-ion batteries

Highly Efficient Interface Modification between Poly(Propylene Carbonate)-Based Solid Electrolytes and a Lithium Anode by Facile Graphite Coating

Uncovering the Function of a Five‐Membered Heterocyclic Solvent‐Based Electrolyte for Graphite Anode at Subzero Temperature

Isotropic Structure and Polymer Interface Intensified Lithium-Ion Transmission in Spherical Graphite Tailings/Coke Composite Anode

A novel approach for synthesis of expanded graphite and its enhanced lithium storage properties

(Digital Presentation) Investigation of Solid Electrolyte Interphase Formation on Highly Oriented Pyrolytic Graphite Anodes in Lithium-Ion Batteries

Molecular Adsorption‐Induced Interfacial Solvation Regulation to Stabilize Graphite Anode in Ethylene Carbonate‐Free Electrolytes

Constructing a universal artificial polymeric ionic liquid interfacial film for graphite anode and High-Voltage cathode

Graphitic carbon nitride (g-C3N4) as an electrolyte additive boosts fast-charging and stable cycling of graphite anodes for Li-ion batteries

Controllable solid electrolyte interphase precursor for stabilizing natural graphite anode in lithium ion batteries

Inhibiting Solvent Co‐Intercalation in a Graphite Anode by a Localized High‐Concentration Electrolyte in Fast‐Charging Batteries

Electrolytes Polymerization‐Induced Cathode‐Electrolyte‐Interphase for High Voltage Lithium‐Ion Batteries