Preparation of Ta-based Layer on SS316N As Bipolar Plate of High Temperature Proton Exchange Membrane Fuel Cells by Molten Salts Disproportionation Reaction

Feng Xiong,Hao Deng,Ruoyin Luo,Shaojie Gao,Chenming Fan,Xin Gao,Bing Li
DOI: https://doi.org/10.1016/j.ceramint.2024.05.344
IF: 5.532
2024-01-01
Ceramics International
Abstract:In this study, a dense Ta-based layer with a thickness of 400 nm was fabricated on SS316N bipolar plates (Ta-SS316N) by using a disproportionation reaction of Ta in a K2TaF7-Ta( powders)-KCl-NaCl molten salt system at 900 °C for 6 h. According to XRD analysis, the Ta-based layer was mainly composed of metallic Ta as well as Ta2N0.86. In the simulated HT-PEMFC cathode environment, the corrosion current density of Ta-SS316N obtained from the potentiodynamicl polarization curves was 0.96 μA/cm2, which meets the 2025 U.S. DOE standard. Compared to the SS316N substrate, Ta-SS316N showed two orders of magnitude higher corrosion resistance and nearly 1 V higher self-corrosion potential, with an interfacial contact resistance of 27.5 mΩ∙cm2, accounting for about one-quarter that of SS316N substrate. This provides a low-cost, easy-to-operate method to prepare Ta-based layer on stainless steel bipolar plates used for HT-PEMFC.
What problem does this paper attempt to address?