NbC/Nb Film-Modified Stainless Steel Bipolar Plate for Proton Exchange Membrane Fuel Cell

Hao Deng,Guoqing Liu,Wei Du,Yi Sun,Chengwei Deng,Bing Li

DOI: https://doi.org/10.5006/4028

2022-01-01

CORROSION

Abstract:The NbC/Nb composite film on SS304 as the bipolar plate of proton exchange membrane fuel cell (PEMFC) was prepared by magnetron sputtering deposition. Scanning electron microscopy and x-ray diffraction were used to characterize the morphology and composition of the film. Electrochemical tests under simulated PEMFC operating conditions (pH 3 H2SO4, 0.1 ppm HF at 80 degrees C) show that the NbC/Nb composite film can provide better corrosion resistance. Potentiodynamic polarization tests reveal that NbC/Nb/SS304 shows lower corrosion current density and more positive corrosion potential than Nb/SS304 and SS304 substrate in simulated PEMFC environments. Potentiostatic tests were also performed at the potentials of 0.84 V-SHE for 24 h to simulate the cathodic PEMFC conditions. NbC/Nb/SS304 reaches the lowest polarization current density of 1.01 x 10(-7)A/cm(2), which is lower than Nb/SS304 (1.83 x 10(-7) A/cm(2)) and SS304 (1.11 x 10(-4) A/cm(2), four orders of magnitude as low). Under the pressure of 140 N/cm(2), the interfacial contact resistance value of NbC/Nb/SS is 8.76 m Omega.cm(2), which is significantly lower than Nb/SS304 (14.0 m Omega.cm(2)) and SS304 substrate (224 m Omega.cm(2)). After 0.84 V-SHE potentiostatic polarization for 24 h, NbC/Nb/SS304 increase by just 0.42 m Omega.cm(2) (from 8.76 m Omega.cm(2) to 9.18 m Omega.cm(2)). However, Nb/SS304 increase by 1.2 m Omega.cm(2) (from 14.0 m Omega.cm(2) to 15.2 m Omega.cm(2)) and SS304 increase by 64 m Omega.cm(2) (from 224 m Omega.cm(2) to 288 m Omega.cm(2)). Moreover, the hydrophobic angle of NbC/Nb/SS304 is 116.5 degrees, compared to Nb/SS304 (108.8 degrees) and SS304 substrate SS304 (67.5 degrees), which is beneficial to the drainage of the PEMFC.