Milling Force And Surface Topography Of Ti-6Al-4V Titanium Alloy Cladded By The Laser
TAO WANG,YANG LI,JIAQI LIU,LINGCHAO QIN,NING WANG,LIFENG ZHANG,HAO WANG,ZHAN LI,Tao Wang,Yang Li,Jiaqi Liu,Lingchao Qin,Ning Wang,Lifeng Zhang,Hao Wang,Zhan Li
DOI: https://doi.org/10.1142/S0218625X18501858
2019-10-07
Surface Review and Letters
Abstract:Surface Review and Letters, Ahead of Print. After the damaged blade is repaired by laser cladding, the quality of the recontouring by milling determines its working performance in reservice. Ti-6Al-4V, titanium alloy, commonly used as the material of manufacturing aero-engine blades, is selected as the experiment material. Laser cladding technology is used to prepare a cladding layer, and milling experiments are carried out on the cladding layer. The effects of milling process parameters on the milling force, roughness, and surface topography are studied. The results show that when the milling speed ([math]) increases to 50[math]m/min, the milling force and roughness ([math]) reach the maximum and at this moment the surface topography is the worst. Afterwards, with an increase in [math], both the milling force and [math] decrease in proportion, and the surface topography also becomes better. As the feed per tooth ([math]) increases, the milling force and [math] also increase. However, the increasing trend gradually slows down. After [math] increases to 0.08[math]mm/z, the milling force and [math] almost no longer increase and the surface topography remains almost unchanged. With an increase in milling width ([math]), the milling force and [math] increase on the whole. But while [math] increases from 0.4[math]mm to 0.8[math]mm, the milling force and [math] increase very slowly. When [math] reaches over 0.8[math]mm, the milling force and [math] increase rapidly again. As [math] changes, the surface topography changes according to the milling force and roughness. On this basis, it is found that while machining a laser cladding layer, the milling force directly affects the surface roughness and topography. Therefore, by adjusting [math], [math], and [math], one can obtain the small milling force and good milling surface of the laser cladding TC4 layer.
chemistry, physical,physics, condensed matter