Electrochemistry-informed Electrochemical Machining (ECM) and Microstructure-Determined Flattening Mechanism of Inconel 738 Superalloy

Yuhan Xing,Yingyue Yin,Fulan Wei,Xiaoni Ma,Shuo Zang,Jianhua Zhang,Shuaihang Pan,Xiaoming Yue
DOI: https://doi.org/10.1007/s00170-024-13758-7
IF: 3.563
2024-01-01
The International Journal of Advanced Manufacturing Technology
Abstract:For nickel (Ni) superalloys, including Inconel 738, electrochemical machining (ECM) is commonly used. However, the mechanisms behind ECM surface flattening and improved surface quality have not been fully elucidated, and the relationship between corrosion and ECM is weakly established without microstructural correlation. To bridge this knowledge gap, we have systematically investigated the electrochemical dissolution behavior of wrought Inconel 738 superalloy in the selected NaNO3 solution and narrowed down the optimal ECM parameters (i.e., 12 V, 0.8 mm/min, and 0.8 MPa). The results show that the precipitates and secondary phases of the Inconel 738 superalloy dominate the final surface quality and the ECM efficiency. Importantly, we have confirmed that a core–shell precipitate phase with shell-layer Ti and Mo enrichment remains on the surface even after the 12 V ECM, limiting the final roughness. This novel finding clarifies why the morphology differs under two representative conditions (i.e., anodic dissolution at 1.3 V, 1500 s and optimal ECM with 12 V, 0.8 mm/min, and 0.8 MPa), and how the core–shell precipitates evolve during the non-equilibrium 12-V ECM condition leads to a totally different flattening process. This ECM analysis method, with solid electrochemical theory and detailed microstructural investigation, reveals the microstructure-dependent ECM flattening mechanisms at precipitate scale and demonstrates how the microstructures influence the ECM processing quality. This novel finding plays a guiding role in improving the quality of ECM processing, shows great value for various industrial applications, and helps strategically break the current surface roughness limit.
What problem does this paper attempt to address?