Corrosion mechanism of the low-GWP fluorinated gas HFO-1234yf with typical aircraft magnesium alloy materials AZ80A
Huilin Bai,Xin Huang,Wei Yuan,Xiaomeng Zhou
DOI: https://doi.org/10.1016/j.engfailanal.2023.107202
IF: 4
2023-05-18
Engineering Failure Analysis
Abstract:The seals are usually used to fill the gap between the fire extinguishing agent and storage containers or discharge pipes in the built-in fire extinguishing system of the aircraft. These seals inevitably touch the fire extinguishing agents, which may reduce the hermeticity of seals. In this paper, the compatibility experiment of 2-bromo-3,3,3-trifluoropropene, a new clean fire extinguishing agent, with fluorosilicone rubber and fluoro rubber was performed at 25 °C, 0.1Mpa. The volume, weight, hardness, and mechanical properties of the sealings were tested, and the changes in cross-section and infrared spectrum were analyzed. The results show that during the contact with 2-bromo-3,3,3-trifluoropropene, fluoro rubber is damaged more severely than fluorosilicone rubber, the shore A hardness measured directly and after drying decreased by 12.9% and 17.6% respectively, while the tensile strength decreased by 51.2% and 86.1% respectively. It is proved that 2-bromo-3,3,3-trifluoropropene have poor compatibility with the fluoro rubber and fluorosilicone rubber.
engineering, mechanical,materials science, characterization & testing