Abstract:Titanium and its alloys have superior electrochemical properties compared to other alloy systems due to the formation of a protective TiO2 film on metal surfaces. The ability to generate the protective oxide layer will depend upon the type of alloy to be used. The aim of this work was to characterize the electrochemical corrosion behavior of titanium Ti-CP2 and alloys Ti-6Al-2Sn-4Zr-2Mo, Ti-6Al-4V, and Ti Beta-C. Samples were anodized in 1 M H2SO4 and H3PO4 solutions with a current density of 0.025 A/cm2. Electrochemical tests on anodized alloys were carried out using a three-electrode cell and exposed in two electrolytes, i.e., 3.5 wt % NaCl and 3.5 wt % H2SO4 solutions at room temperature. Scanning electron microscopy (SEM) was used to observe the morphology of anodized surfaces. The electrochemical techniques used were cyclic potentiodynamic polarization (CPP) and electrochemical noise (EN), based on the ASTM-G61 and G199 standards. Regarding EN, two methods of data analysis were used: the frequency domain (power spectral density, PSD) and time-frequency domain (discrete wavelet transform). For non-anodized alloys, the results by CCP and EN indicate icorr values of ×10−6 A/cm2. However, under anodizing conditions, the icorr values vary from ×10−7 to ×10−9 A/cm2. The PSD Ψ0 values are higher for non-anodized alloys, while in anodized conditions, the values range from −138/−122 dBi (A2·Hz−1)1/2 to −131/−180 dBi (A2·Hz−1)1/2. Furthermore, the results indicated that the alloys anodized in the H3PO4 bath showed an electrochemical behavior that can be associated with a more homogeneous passive layer when exposed to the 3.5 wt % NaCl electrolyte. Alloys containing more beta-phase stabilizers formed a less homogeneous anodized layer. These alloys are widely used in aeronautical applications; thus, it is essential that these alloys have excellent corrosion performance in chloride and acid rain environments.

Localised instability of titanium during its erosion-corrosion in simulated acidic hydrometallurgical slurries

Research development of corrosion of titanium in the oral bioenvironment

Influence of microstructure on the erosion and erosion–corrosion characteristics of 316 stainless steel

Surface Properties and Erosion–Corrosion Behavior of Nanostructured Pure Titanium in Simulated Body Fluid

Electrochemical Corrosion of Titanium and Titanium Alloys Anodized in H2SO4 and H3PO4 Solutions

Local Fine Structural Insight into Mechanism of Electrochemical Passivation of Titanium.

Research progress on the corrosion behavior of titanium alloys

The role of titanium in the initiation of localized corrosion of stainless steel 444

Reactivity of submicrocrystalline titanium: II. Electrochemical properties and corrosion stability in sulfuric acid solutions

Influence of Cupric, Ferric, and Chloride on the Corrosion of Titanium in Sulfuric Acid Solutions Up to 85°C

Corrosion of titanium: Part 1: aggressive environments and main forms of degradation

Distinct phase-selective corrosions of Ti-48Al alloy in aqueous electrolyte and molten salt

(Digital Presentation) Corrosion-Resistance Investigation of Titanium Passive Layer in Acidic Solution

Impact of simulated inflammation and food breakdown on the synergistic interaction between corrosion and wear on titanium

Electrochemical anodizing treatment to enhance localized corrosion resistance of pure titanium

New insights into the mechanism of localised corrosion induced by TiN-containing inclusions in high strength low alloy steel

Study on Chemical Corrosion Properties of Titanium Alloy in 2A14 Aluminum Melt

Stress corrosion cracking of the titanium alloys under hydrostatic pressure resulting from the degradation of passive films

(Digital Presentation) Anti-Corrosion Investigation of Titanium Electrode for Cu Plating

Electrochemical Evaluation of Stress Corrosion Cracking Susceptibility of Ti-6Al-3Nb-2Zr-1Mo Alloy Welded Joint in Simulated Deep-Sea Environment

Elucidating the effect of titanium alloying on the pitting corrosion of ferritic stainless steel