Abstract:To enhance the corrosion resistance, biocompatibility and mechanical durability of biomedical titanium alloys, a novel β-Ta2O5 nanoceramic coating was developed using a double glow discharge plasma technique. The surface morphology, phase composition and microstructure of the as-deposited coating were examined by atomic force microscopy (AFM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The coating exhibits a striated structural pattern along the growth direction, which consists of equiaxed β-Ta2O5 grains, 15-20 nm in diameter in cross-section, showing a strong (001) preferred orientation. The mechanical properties and contact damage resistance of the β-Ta2O5 coating were evaluated by nanoindentation. Additionally, scratch tests were performed to evaluate the adhesion strength between the β-Ta2O5 coating and the Ti-6Al-4V substrate. The β-Ta2O5 coating shows high hardness combined with good resistance to both indentation and scratch damage, thus favoring it for long-term load-bearing application in the human body. Electrochemical behavior of the coating was analyzed in both a 0.9 wt % NaCl solution and Ringer's solution at 37 °C, by various electrochemical analytical techniques, including potentiodynamic polarization, electrochemical impedance spectroscopy, potential of zero charge and Mott-Schottky analysis. Compared with uncoated Ti-6Al-4V and commercially pure tantalum, the β-Ta2O5 coating possesses a more positive Ecorr and lower icorr in both aqueous solutions, which is attributed to the thicker and denser β-Ta2O5 coating that provides more effective protection against corrosive attack. In addition, the β-Ta2O5 coating shows stable impedance behavior over 5 days immersion under both simulated body solutions, corroborated by the capacitance and resistance values extracted from the EIS data. Mott-Schottky analysis reveals that the β-Ta2O5 coating shows n-type semiconductor behavior and its donor density is independent of immersion time in both aqueous solutions. Its donor density is of the order of 1 × 1019 cm-3, which is an order of magnitude less than that of the passive films formed on either commercially pure Ta or uncoated Ti-6Al-4V. Moreover, according to the differences between corrosion potential and potential of zero charge, the β-Ta2O5 coating exhibits a greater propensity to repulse chloride ions than both commercially pure Ta and uncoated Ti-6Al-4V. Therefore, the newly developed coating could be used to protect the surface of biomedical titanium alloys under harsh conditions.

Surface Properties and Erosion–Corrosion Behavior of Nanostructured Pure Titanium in Simulated Body Fluid

Improving Pure Titanium's Biological and Mechanical Characteristics through ECAP and Micro-Arc Oxidation Processes

Tribocorrosion behaviour of porous anatase and rutile phases formed on surface of anodised Ti45Nb alloy

On the Optimization of Roughness and Corrosion Resistance of Laser Beam Powder Bed Fusion Fabricated Ti–6Al–4V Parts—An Electrochemical Approach

Electrochemical Properties of a Novel Β-Ta2o5 Nanoceramic Coating Exposed to Simulated Body Solutions.

Influence of Surface Nano-Structuring on Microstructure, Corrosion Behavior and Osteoblast Response of Commercially Pure Titanium Treated Through Ultrasonic Shot Peening

Influence of micro and nanoporous TiO 2 surface modifications on physical-chemical and biological interactions

Effect of Ultrasonic Surface Mechanical Attrition Treatment-Induced Nanograins on the Mechanical Properties and Biocompatibility of Pure Titanium

Corrosion Behavior of Titanium Alloys (Ti CP2, Ti-6Al-2Sn-4Zr-2Mo, Ti-6Al-4V y Ti Beta-C) with Anodized and Exposed in NaCl and H2SO4 Solutions

Corrosion and wear behavior of Ti-5Cu-xNb biomedical alloy in simulated body fluid for dental implant applications

Effects of Pulsed Laser Irradiation on Commercially Pure Titanium: Mechanical Properties and Corrosion Resistance in a Salty Environment

Electrochemical behavior of nano and femtosecond laser textured titanium alloy for implant surface modification

Wear and Failure Analysis of Ti-6Al-4V Titanium Alloy with a Protective Coating during High-Speed Erosion

Study the Effect of Surface Parameters Variation on the Corrosion Behavior of Thin Chromium Layer on Modified Titanium

Residual stress, fatigue behavior, and mechanical properties of equal-channel angular pressed commercial pure titanium

Mechanical, corrosion, nanotribological, and biocompatibility properties of equal channel angular pressed Ti-28Nb-35.4Zr alloys for biomedical applications

Influence of Surface Modification of Titanium and Its Alloys for Medical Implants on Their Corrosion Behavior

Electrochemical Corrosion of Titanium and Titanium Alloys Anodized in H2SO4 and H3PO4 Solutions

Study on electrochemical polishing mechanism of TC4 titanium alloy

Optical and Corrosion Studies of Spray Pyrolysis Coated Titanium Dioxide Thin Films

Surface modification of titanium by anodic oxidation in phosphoric acid at low potentials. Part 2. In vitro and in vivo study