Enhancing Mg 2+ and Mg 2+ /Li + Storage by Introducing Active Defect Sites and Edge Surfaces in MoSe 2

Jingdong Yang,Jinxing Wang,Ling Zhu,Xiao Wang,Xiaoyang Dong,Wen Zeng,Jingfeng Wang,Fusheng Pan

DOI: https://doi.org/10.1002/celc.202101066

IF: 4

2021-10-26

ChemElectroChem

Abstract:Recently, Mg ion batteries (MIBs) and Mg-Li hybrid ion batteries (MLIBs) are deemed as the potential energy storage devices. However, due to insufficient storage sites of Mg 2 + in cathode, MIBs show low reversible capacity. For MLIBs, the property is also seriously restricted due to the main Li + intercalation reaction and less Mg 2+ intercalation reaction. Herein, ultrathin MoSe 2 nanosheets with enriched atomic defects and exposed edge surfaces are prepared by hydrothermal method and subsequent hydrogen treatment. It is found that the Mg 2+ storage performance is markedly enhanced, and Mg 2+ /Li + co-intercalation can be achieved. Density functional theory (DFT) calculation shows that, by introducing a large number of atomic defects and edge exposed surfaces in the ultrathin MoSe 2 nanosheets, the Mg 2+ storage sites are increased, and the diffusion and migration ability of Mg 2+ and Li + are improved, resulting in a significant property improvement. Further, the Mg 2+ intercalation in MIBs and Mg 2+ /Li + co-intercalation in MLIBs are confirmed. The discharge-charge mechanisms only based on the intercalation reactions for both MIBs and MLIBs are also revealed.

electrochemistry