Abstract:Cross-laminated bamboo (CLB) is a bamboo-based construction product with bamboo's advantages, which are green, environmentally protective, and sustainable. However, bamboo is easy to crack. Structural elements in bamboo constructions are assembled onsite, making splitting cracks easily form at joints and bolt connections. Therefore, it is essential to assess cracked structure safety with fracture mechanics. However, rare studies are addressed on fracture properties of bidirectional laminated bamboo, especially the translaminar fracture resistance, which represents the ability to arrest a catastrophic crack in structures. This paper studies the translaminar fracture properties of CLB composite using three-point bending beam tests. Load-displacement and load-CMOD curve characteristics, fracture process, and the failure modes of bidirectional laminated bamboo are analyzed. The R-curve expressed by the energy release rate is calculated by three methods. Results demonstrate that the Rcurves obtained by the three different methods show similar results. The methods to determine R-curves employed in this study are simple and can describe the translaminar fracture toughness of laminated bamboo. The methods are validated by comparing the traction-separation relations calculated from the R-curves to those measured by double-edge notched tests (DENT). A comparison of the bidirectional laminated bamboo's energy release rate to the matrix-dominated energy release rate of unidirectional laminated bamboo reveals that bidirectional fiber arrangement has a remarkable improvement on the toughening of laminated bamboo at and after crack initiation. Moreover, the lay-up effects of CLB are analyzed by relating the energy release rate results to the failure pattern of fractured specimens. It is found that fiber pullout/bridging caused by 90 degrees direction crack propagation around fiber bundles is the dominant toughening mechanism of CLB. The lay-up sequence of 0 degrees and 90 degrees plies also has an effect on 90 degrees direction crack propagation; therefore, it will influence the toughness of CLB.

Experimental Research on the Fracture of Laminated Bamboo Lumber Using Compact Tension Specimens Based on the Net Section Method and Digital Image Correlation Technique

Experimental investigation on shear behavior of full-scale glued laminated bamboo beams under three-point loading test and using digital image correlation technique

Crack Propagation And Fracture Process Zone (Fpz) Of Wood In The Longitudinal Direction Determined Using Digital Image Correlation (Dic) Technique

Effect of crack size, thickness and span on the transverse mode I fracture characteristics of laminated flattened-bamboo lumber

Mechanical Behavior of Glued Laminated Bamboo Moment-Resisting Connections

Experimental study on mechanical behavior of glue laminated bamboo Ⅰ-joists

Mode I Fracture Behavior of Unidirectional Bamboo Laminate and Its Applications to the Estimation of Bamboo-Steel-bamboo Connections’ Bearing Capacities

Experimental investigation on the fracture toughness of Z-pins reinforced composite laminates

Experimental Investigation on Translaminar Fracture Behavior of Cross-Laminated Bamboo

Determination and influential factors of fracture toughness in unidirectional laminated bamboo-composite using double cantilever beams and single-edge notched bend tests

Experimental Study of the Fracture Behavior of Bamboo Under Tension Based on Digital Speckle Correlation Method

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

Comparative Study of Toughness and Energy Evaluation of Laminated Bamboo Composites and Toughening Mechanism

Experimental Investigation Of The Mixed-Mode Crack Expanding In Bamboo

Experimental and Numerical Investigations on the Mode I Delamination Growth Behavior of Reinforced Laminates Via a ZPI (Z-Pin Pre-Hole Insertion) Technique

Research on Moso Bamboo Radical Fracture Toughness

Tangential Fracture Toughness of Bamboo

Experimental and numerical studies of brittle rock-like specimens with unfilled cross fissures under uniaxial compression

Experiments on Laminated Bamboo Lumber Nailed Connections

Translaminar Mode-I Fracture Toughness Experiment of Pultruded GFRP Laminates Using Extended Compact Tension Specimen

Experimental Data on Fracture of Open-Hole Composite Laminates Subjected to Tension Loading