Valorisation of corn waste as fiber, biosilica, and their epoxy composites: fatigue, fracture toughness, water absorption, and drilling properties
Manigandan P.,Senthil Vadivu K,Veera Prabakaran Elanjeitsenni,Arul Jothi G
DOI: https://doi.org/10.1007/s13399-024-06306-6
IF: 4.05
2024-11-08
Biomass Conversion and Biorefinery
Abstract:Heavy metal-based vehicle caused increase in fuel consumption, which creates pollution in the environment; thus, scientists across the nation researched to produce light weight, cost-effective, easy degradable, corrosive resistant composite material. Due to such features present in the composite material, the present research aims to examine the impact of alkali-silane treatment on the time-dependent and machining behavior of composites. Further, the alkali treatment and silane treatment on fiber and filler particle are carried out to provide even dispersion of filler particle and better reinforcement and interfacial bonding adhesion to the composite material, which makes a novelty to this study. The obtained fiber and filler particle were reinforced to matrix by using hand layup method and subsequently cured. This prepared composite material's strength is analyzed as per the ASTM standards. The results indicate that the inclusion of surface modified corn-fiber reinforced EF composite shows stronger interfacial adhesion, which implies loss factor of 42.8% lower than neat epoxy. Similarly, reinforcing corn husk fiber increases the energy release rate by 2500% and the fracture toughness by 156.47% when compared to pure epoxy composite. Further, the inclusion of biosilica particle of 2.0 vol.% exhibited the highest storage modulus of 5.69 GPa and the lowest loss factor of 0.32. This demonstrates the beneficial effect of combining alkali and silane treatment on corn fiber and filler particle. The epoxy composite (EFP3) of chemically treated fiber 30 vol.% and 2 vol.% of biosilica reinforcement exhibits a higher fatigue life cycle, fracture toughness, and energy release rate of 30,546, 26.5 MPa√m, and 0.86 MJ/m 2 , respectively. Similarly, the composite designation EFP3 has the lowest contact angle of 78°, indicating the preserved hydrophobicity. A drilling study has shown that using a 4-mm drill bit and 8-mm drill bit. The resultant of the drilling studies concludes that the use of 2.0 vol.% biosilica reduced the occurrence of fiber pull-out while drilling. Owing to such improved strength properties, light weight, corrosive resistant features in the biocomposite are applied in industries such as automotive, sporting goods, food and drug packaging, aerospace, and other technical applications that require strong load-bearing capacity, etc.
energy & fuels,engineering, chemical