Structural and Photoluminescence Characteristics of a Novel Single-Phase White-Emitting Phosphor SrBi₂Nb₂O₉:Dy<SUP>3+</SUP>

Xiao Yang,Ruirui Cui,Jun Zhang,Chaoyong Deng

DOI: https://doi.org/10.1002/pssb.202400049

2024-01-01

physica status solidi (b)

Abstract:A group of white light-emitting phosphors SrBi2Nb2O9:xDy(3+) (SBN:xDy(3+)) are prepared by high-temperature solid reaction. The crystal phase, morphology, and photoluminescence (PL) characteristics of the prepared SBN:xDy(3+) are analyzed. The X-ray diffraction results prove that the synthesized samples are pure phase, in which the shift of the main peak depicted that crystal interplanar distance decreases after Dy3+ replacing Bi3+. The scanning electron microscope results show that the average crystal size of the sample is approximate to 1-10 mu m. Energy dispersive X-ray spectroscopy shows that the ratio of element composition of the SBN:xDy(3+) is similar to the theoretical calculation. The PL excitation illustrates the excitation peaks mainly exist at 389, 399, 426, and 450 nm due to the transitions of Dy3+. For PL, the emission peaks of samples with different doping concentrations are centered at 479 and 573 nm. The ratio of yellow intensity to blue intensity indicates that Dy3+ is located at a high symmetry site, which has the possibility to produce suitable white light. The Commission Internationale de l'Eclairage coordinates of the SBN:xDy(3+) are located near the standard white light coordinate. All these results prove that SrBi2Nb2O9:xDy(3+) can be a potential material in the white light application.