Optimizing strength and fatigue crack propagation resistance of in-situ TiB 2 /Al-Cu-Mg composite sheet
Qingqing Pu,Zhiping Wang,Tai Luo,Yugang Li,Jiwei Geng,Peikang Xia,Xianfeng Li,Dong Chen,Hongze Wang,Haowei Wang
DOI: https://doi.org/10.1016/j.ijfatigue.2023.108058
IF: 5.489
2023-11-10
International Journal of Fatigue
Abstract:The industrial-grade TiB 2 /Al-Cu-Mg composite sheet was fabricated via casting and rolling methods. Cold-rolling coupled with low-temperature aging treatment was used to regulate the grain size, dislocation density, precipitates and TiB 2 particle distribution, to optimize the strength and fatigue crack propagation (FCP) resistance of the sheet. The results show that pre-rolling deformation combined with low-temperature long-term aging is beneficial for obtaining fine grains, high-density dislocations, high-density nano precipitates and uniform particle distribution, all of which are conducive to improving strength. The TiB 2 /Al-Cu-Mg composite sheet can achieve remarkable ultimate tensile strength over 600 MPa regardless of its excellent elongation (12%). Furthermore, uniformly distributed TiB 2 particles and high-density nano precipitates are beneficial for offsetting the negative effect of high-density dislocations on FCP. Finally, the small pre-rolling deformation (5%) combined with low-temperature long-term aging achieves excellent strength and FCP resistance combination.
materials science, multidisciplinary,engineering, mechanical