Experimental Study on Chloride Penetration of the New-to-old Concrete Interface

Juhui Zhang,Yitong Pan,Jing Li,Hui Yun,Zhongguo Guan

DOI: https://doi.org/10.1016/j.conbuildmat.2024.135585

IF: 7.4

2024-01-01

Construction and Building Materials

Abstract:New-to-old concrete interfaces are commonly found in reinforced concrete (RC) structures due to precast splices, repairs, and construction joints. The interfaces provide access for chloride ions, oxygen, and water, which intrude on the concrete, reducing its durability with new-to-old concrete interfaces. Although the mechanical bonding properties of new-to-old concrete interfaces have been extensively studied, there is a notable gap in the durability of old-new concrete, particularly concerning chloride ion penetration resistance. This paper examined the interface bonding properties and the chloride ion penetration resistance of old-new concrete through ultrasonic nondestructive testing and rapid chloride migration (RCM) tests. Influences of water-cement ratio, casting interval, and interface treatment were considered. The test results indicated that the interface treatment has minimal effect on ultrasonic velocity while the w/c ratio is the primary factor influencing ultrasonic velocity. The bonding quality of the interface between new and old concrete is more accurately reflected by ultrasonic velocity than by the amplitude of the first wave. The chloride penetration in the old and new concrete specimens is primarily influenced by the water-cement ratio and curing age. As the casting interval increases, the difference in the chloride penetration between the new concrete area and the old concrete area becomes more pronounced. When the strength of new concrete exceeds that of old concrete, the chloride penetration at the interface is primarily influenced by the characteristics of the old concrete. The difference in chloride migration coefficients between the interface and new concrete ranges from 40% to 54%, while the difference between the interface and old concrete is only 4.5–22.2%. However, when the new and old concrete has the same strength, the chloride penetration at the interface tends to be closer to that of new concrete. The impact of interface treatment on the depth of chloride penetration is minimal. An influence coefficient was proposed to assess the effect of the interface on the chloride penetration resistance. With a shorter casting interval, the chloride ion penetration resistance is more affected by different interface treatments. As the casting interval increases, this influence gradually diminishes.