Abstract:In reinforced concrete (RC) structures, new-to-old concrete interfaces are widely present due to precast splices, repairs, and construction joints. In this paper, both monolithic and segmental specimens were fabricated with five kinds of water–cement ratios, including ordinary and high-strength concrete. The impressed current-accelerated corrosion test was used, and the degree of reinforcement corrosion was controlled by Faraday's Law. In the accelerated corrosion process, the concrete surface cracking, steel corrosion, and mechanical properties of the corroded steels in the segmental specimens were investigated and compared with monolithic specimens considering the pouring method, concrete strength, and the strength difference between new and old concrete. The prediction of concrete cracking time was also discussed. The results indicated that, for the monolithic specimens, longitudinal cracks could be observed on the ordinary concrete surface, while no cracks were produced on a high-strength concrete surface; only the rust leaked out at the ends. For the segmental specimens, both longitudinal and transverse cracks were produced on an ordinary concrete surface, while only transverse cracks were produced at the high-strength new-to-old concrete interfaces. The steel embedded in the segmental specimens suffered more sectional loss at the new-to-old concrete interfaces. An influence coefficient based on the section loss of the rebar was proposed to evaluate the influence of interfaces on the rust uniformity of rebars. When there were differences in strength between new and old concrete, the influence of the interface on the uniformity of steel bar cross-section loss slightly increased. Based on available theoretical analysis for uniform corrosion, the concrete cracking time of the monolithic specimens was predicted, which was basically consistent with experimental phenomena. However, further research is needed to predict the service life of segmental specimens with new-to-old concrete interfaces.

Chloride transport through the interface in repaired marine concrete systems in a cracked state

Effect of chloride penetration on CFRP sheet, CFRP‐concrete interface, and CFRP‐strengthened concrete beams

Experimental and Numerical Study on the Microstructure and Chloride Ion Transport Behavior of Concrete-to-concrete Interface

Chloride Penetration in Surface-Treated Concrete in Natural and Accelerated Environments

Analysis of Initial Cracking of an Interface between a Bundled Lipped Channel-Concrete Composite Wall and an Infill Wall

Investigating the Self-Healing Performance of Cracked Undersea Constructions

Chloride Penetration into Concrete Damaged by Uniaxial Tensile Fatigue Loading

InfIuence of Ioad crack on chIoride diffusion in concrete

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Evaluating the Chloride Permeability of Steel-Concrete Interface Based on Concretes of Different Stability

Concrete Cover Cracking and Reinforcement Corrosion Behavior in Concrete with New-to-Old Concrete Interfaces

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

Chloride Transport Behavior in Bending-Shear Section of Reinforced Concrete Beam under Combined Effect of Load and Environment

Comparative Analysis of Microdamage-affected Chloride Transport in Concrete under Static and Dynamic Hydraulic Pressure

Experiments of chloride ingression in flexural reinforced concrete beams

Chloride Transport in Interfacial Zone of New–Old Concrete Joints of Precast Prestressed Concrete Bridges under Fatigue Load

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Influence of Crack Width on Chloride Penetration in Concrete Subjected to Alternating Wetting–Drying Cycles

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Modeling of chloride ions diffusion in cracked concrete