Effect of Superheat on the Initial Solidification Behaviors of 3.5 wt pct Si Non-oriented Electrical Steel During Strip Casting

Lulu Song,Wanlin Wang,Qingxiao Feng,Xueying Lyu,Yunli Zhang,Jingzhou Lu,Liguang Liang,Jie Zeng,Chenyang Zhu

DOI: https://doi.org/10.1007/s11663-024-03015-3

2024-01-01

Metallurgical and Materials Transactions B

Abstract:In this study, 3.5 wt pct Si as-cast strips were prepared at various casting superheat (20 °C, 67 °C, 104 °C, and 120 °C) using a dip test apparatus. Detailed investigations of the microstructure, texture, and inclusions of as-cast strips were conducted using optical microscopy, electron backscatter diffraction, and scanning electron microscopy. In addition, the effect of casting superheat on the solidification point during the strip-casting process was simulated using the ProCast model. The findings indicate that, at a low superheat of 20 °C, the as-cast strips exhibited equiaxed crystal microstructures with weak texture and an average grain size of around 186 μm. Conversely, a high superheat of 104 °C resulted in well-developed columnar crystal microstructures, exhibiting an average grain size of approximately 278 μm and a favorable {100} texture ratio of up to 78.2 pct. Furthermore, the inclusions in the cast strips were identified as composite inclusions of Al 2 O 3 -SiO 2 -AlN with average diameters increased from 0.92 μm at a superheat of 20 °C to 1.24 and 1.68 μm at superheats of 67 °C and 104 °C, respectively. ProCast simulation revealed a decrease in the solidification point as the superheat increased. However, at a superheat of 120 °C, the solidification point fell below the exit position, rendering the incomplete solidification. The optimal superheat for casting 3.5 wt pct Si electrical steel is 104 °C.