Abstract:Continuous casting was simulated on a modified unidirectional solidification setup by functionally controlling the centerline temperature of slab and stirring intensity to optimize continuous casting process. Experimental results indicated that the simulated solidification structure is almost the same with the actual one of continuous casting billet. The ratio of equiaxed grain increased from 19% to 58% dramatically with stirring intensity increasing from Orpm to 80rpm. Meanwhile, the secondary dendrite arm spacing decreased. The carbon macro-segregation reduced and the carbon element distributed more homogeneous with CET occurring. That is, the solidification structure can be considerably improved and composition segregation is reduced using stirring during our experiments. Additionally, the stirring mechanism on solidification structure and carbon macro-segregation was discussed.

Effect of stirring on the solidification structure and segregation of 60Si2MnA spring steel during continuous casting