Abstract:The aim of this study is to determine the effect of changes in the phase composition of Al2O3–Si3N4 ceramics that were obtained using the method of mechanochemical solid-phase grinding on their resistance to the process of long-term thermal exposure, accompanied by the processes of oxidation and softening. The relevance of this research consists of determining the influence of the phase composition of ceramics on the change in their strength and thermophysical parameters, on the basis of which, we can draw a conclusion about the optimal composition of composite ceramics that have great prospects in the field of fire-resistant, heat-resistant, or radiation-resistant structural materials. During this study, the dynamics of the changes in the phase transformations of the xAl2O3–(1−x)Si3N4 ceramics, with variations in the ratio of the components, initiated by the thermal annealing of the samples, was established. According to the assessment of the phase transformations with variations in the ratio of the components, it was found that thermal annealing in an air environment at an Al2O3 concentration in the order of 0.3–0.5 M leads to the formation of an orthorhombic Al2(SiO4)O phase and an elevation in its contribution at concentrations above 0.5 M, which causes a rise in the thermophysical parameters and resistance to high-temperature degradation. During the heat resistance tests, it was found that the formation of the composite ceramics with the Si3N4(SiO2)/Al2(SiO4)O/Al2O3 phase composition results in an increase in the stability of their strength properties when exposed to thermally induced oxidation, which has a negative impact on their resistance to softening and a decrease in hardness. Moreover, the presence of the Al2(SiO4)O phase in the composition of the ceramics causes a slowdown in the processes of thermal oxidation of the Si3N4 phase under prolonged temperature exposure, alongside an increase in the degradation resistance of strength properties by more than 4–7 times, in comparison with the softening data established for single-component ceramics.

Study of the effect of synthesis temperature and thermal aging on structural, dielectric properties and phase composition in NiO/NiAl2O4 composite ceramics

Effect of Phase Composition Variation of Oxy–Nitride Composite Ceramics on Heat Resistance and Preservation of Strength Parameters

Study of the Aid Effect of CuO-TiO2-Nb2O5 on the Dielectric and Structural Properties of Alumina Ceramics

Study of Annealing Effect Upon the Structural and Solar- Selective Properties of C/Ni/NiO Composite Coatings Prepared by Sol–gel Method

Study of Aging Temperature on the Thermal Compression Behaviors and Microstructure of a Novel Ni-Cr-Co-Based Superalloy

TUDY OF THE INFLUENCE OF THE ACCUMULATED DOSE OF DAMAGE IN THE NEAR-SURFACE LAYER ON RESISTANCE TO EXTERNAL INFLUENCES ASSOCIATED WITH CORROSION PROCESSES DURING HIGH-TEMPERATURE ANNEALING

Effect of aging treatment on microstructure and wear performance of Ni-rich NiTiFe alloy

Hydrothermal stability of CeO2–Al2O3 composites, a structural study and oxygen storage capacities

Synthesis and Characterization of Core-Shell NiO@Al2O3 with High Ni/Al Ratio and High Calcination Temperature

Transformation of oxide nanoparticles in a nickel-based ODS alloy aged at 1000 °C

In situ processing and aging behaviour of an aluminium/Al2O3 composite

Design and synthesis of thermistor materials with high aging stability: Multicomponent equiatomic Mn-Co-Ni-Al-Zn-O ceramics

Impact of Aging Temperature on the Performance of a Nickel-Iron-Based Superalloy

Tribological performance and high temperature oxidation behaviour of thermal sprayed Ni- and NiCrAlY-based composite coatings

High-Temperature Deformation and Creep of Nanostructured Composite Ceramics Based on Aluminum Oxide

Study of High Temperature Oxidation Properties of Al2O3-SiO2 Ceramic Coatings on Nickel Superalloy

Microstructural investigation of the aging behavior of $(3Y-TZP)-Al_2O_3$ composites

Microstructure, Mechanical Properties and High Temperature Tribological Behavior of NiAl-based Composites

Thermal stability of Ni3Al microstructure and microhardness after spark plasma sintering

Effect of aging on temperature dependence of FeCuSiNbB nanocrystalline materials

Preparation and mechanical properties of NiCr-Al 2O 3-ZrO 2(8Y) ceramic composites