Hierarchical Flower-Like Porous Carbon Nanosheets with Richly Exposed (002) Planes for High-Performance Sodium–Ion Batteries

Zhenqian Wu,Xianwei Li,Xudong Ma,Ling Xin,Zhijian Huang,Xiao Yu,Yong Liu

DOI: https://doi.org/10.1021/acsanm.3c04634

IF: 6.14

2024-01-01

ACS Applied Nano Materials

Abstract:Hard carbon is the most promising anode material for sodium-ion batteries (SIBs). However, its electrochemical performance is still unsatisfactory, especially at high-current densities. Herein, we propose a self-assembly strategy to synthesize hierarchical flower-like hard carbon nanosheets with richly exposed (002) planes (HFHCN) and combined micro- and mesopores, which provide more storage sites and faster reaction kinetics than the commercial hard carbon microspheres without pores (CHCM), resulting in better electrochemical performance, especially at high-current densities. The HFHCN electrode achieved a higher charge capacity (390.8 mA h g(-1) at 0.02 A g(-1)) and better rate capability (104.8 mA h g(-1) at 2.0 A g(-1)). With increasing current densities, the HFHCN electrodes maintain an almost unchanged initial Coulomb efficiency and electrochemical polarization and a slowly decreasing charge capacity at the low-voltage plateau, whereas the CHCM electrode shows a drastically deteriorated performance in these aspects. A turning point for their significant difference in electrochemical performance occurs at 0.5 A g(-1), where the charging capacity at the low-voltage plateau is 72 mA h g(-1) for the HFHCN electrode, but 0 for the CHCM electrode. When matched with the NVP (Na3V2(PO4)(3)) cathode, HFHCN parallel to NVP full-cells show a higher initial discharge capacity (273.5 mA h g(-1) at 0.1 A g(-1)) and better rate performance (63.2 mA h g(-1) at 5 A g(-1)) than those of the CHCM parallel to NVP full-cell (180.2 mA h g(-1) at 0.1 A g(-1) and 2.8 mA h g(-1) at 5 A g(-1)). In addition, HFHCN parallel to NVP full-cells also have a longer operating plateau and lower electrochemical polarization than the CHCM parallel to NVP full-cell, which are also the main factors contributing to the higher energy density.