Influence of gradation in the reinforcement particles on the interfacial microstructure and mechanical properties of functionally graded composites

Halil Karakoç,Hanifi Çinici,M. Saravana Kumar,Tolga yılmaz,İsmail Ovalı,Che-Hua Yang,Arun Arjunan,Tolga Yılmaz

DOI: https://doi.org/10.1016/j.mtcomm.2023.107601

IF: 3.8

2023-11-29

Materials Today Communications

Abstract:In this research, Al6061 alloy-based Functionally Graded Composites (FGCs) were fabricated by hot pressing which is composed of 7 layers with different proportions of Al 2 O 3 reinforcement particles. The addition of Al 2 O 3 particles is gradually increasing in the other layers from top to bottom (Layer 1 - Pure Al6061 alloy, Layer 2–5 wt% Al 2 O 3, Layer 3–10 wt% Al 2 O 3, Layer 4–20 wt% Al 2 O 3, Layer 5–30 wt% Al 2 O 3, Layer 6–40 wt% Al 2 O 3, Layer 7–50 wt% Al 2 O 3 ). Moreover, three different Al 2 O 3 particle sizes (8, 16 and 32 μm) were used to fabricate three sets of FGCs. Reciprocating wear studies were performed and the result shows that the FGC with 8 μm Al 2 O 3 particle size shows 85.5% improved wear resistance. Further, various wear mechanisms were investigated and finally compressive strength analysis proved that the homogenous distribution of Al2O3 particles in the FGC with 16 μm Al2O3 particle size helps achieve the maximum compression stress of 476.04 MPa compared with other FGCs.

materials science, multidisciplinary