Mechanisms of Enhanced Thermal Stability of Polarization in Lead-Free (Bi1/2na1/

Zhongming Fan,Lin Zhou,Tae‐Hoon Kim,Ji Zhang,Shan‐Tao Zhang,Xiaoli Tan

DOI: https://doi.org/10.1103/physrevmaterials.3.024402

IF: 3.98

2019-01-01

Physical Review Materials

Abstract:$(\mathrm{B}{\mathrm{i}}_{1/2}\mathrm{N}{\mathrm{a}}_{1/2})\mathrm{Ti}{\mathrm{O}}_{3}$-based solid solutions, one of the major systems of lead-free piezoelectric ceramics, exhibit a low thermal depolarization temperature (${T}_{\mathrm{d}}\ensuremath{\sim}100{\phantom{\rule{0.16em}{0ex}}}^{\ensuremath{\circ}}\mathrm{C}$). It was reported that by incorporating 30 mol% ZnO particles to form a ceramic composite of ${(\mathrm{B}{\mathrm{i}}_{1/2}\mathrm{N}{\mathrm{a}}_{1/2})}_{0.94}\mathrm{B}{\mathrm{a}}_{0.06}\mathrm{Ti}{\mathrm{O}}_{3}$/ZnO, the depolarization process can be shifted up to \ensuremath{\sim}250 \ifmmode^\circ\else\textdegree\fi{}C. In the present work, a variety of advanced transmission electron microscopy techniques, including in situ heating, annular bright-field, high-angle annular dark-field, geometric phase analysis, energy-dispersive spectrum and electron energy-loss spectroscopy, are employed to investigate the underlying mechanisms for the enhanced thermal stability of polarization in the composite. It is found that the abrupt depolarization in ${(\mathrm{B}{\mathrm{i}}_{1/2}\mathrm{N}{\mathrm{a}}_{1/2})}_{0.94}\mathrm{B}{\mathrm{a}}_{0.06}\mathrm{Ti}{\mathrm{O}}_{3}$ at ${T}_{\mathrm{d}}$ becomes diffused over a wide temperature window up to the temperature at maximum dielectric constant (${T}_{\mathrm{m}}$) under the combined actions of the incorporation of Zn into the perovskite lattice, the presence of residual stresses, and the pinning effect on micron-sized domains provided by ZnO particles.