Abstract:Abstract Ce and F were added to MCM-48 molecular sieve by hydrothermal synthesis, and Pd/Ce(F)-MCM-48 metal acid bifunctional catalysts were prepared by impregnation method. The physical and chemical properties of Ce(F)-MCM-48 and Pd/Ce(F)-MCM-48 were characterized by X-ray diffraction, scanning electron microscope, NH 3 temperature programmed desorption instrument, Fourier infrared spectrometer, and X-ray photoelectronic spectrometer characterization methods. The results showed that when the molar ratio of the raw materials was n (Ce): n (TEOS) = 0.02 and n (NaF): n (TEOS) = 0.10, Ce(F)-MCM-48-0.10 molecular sieve had a high degree of order and large specific surface area and pore volume, the total acid content increased, and the acid strength also increased. And it had an acidic center and generated certain oxygen vacancies. The catalyst prepared after Pd impregnation had good dispersibility. 0.4% Pd/Ce(F)-MCM-48-0.10 catalyst still maintained the crystalline phase of MCM-48 molecular sieve. A micro-reaction device was used to examine the catalytic performance of n -heptane isomerization of Pd/Ce(F)-MCM-48-0.10 catalysts. When the hydrogen flow rate was 30 mL·min −1 , reduction temperature was 300°C, reduction time was 4 h, weight hourly space velocity was 7.6 h −1 , and reaction temperature was 280°C, 0.4% Pd/Ce(F)-MCM-48-0.10 catalyst was used in the heptane isomerization reaction, where the conversion of n -heptane was 67.3% and the selectivity of isoheptane was 96.5%.

Study on the Preparation and N-Heptane Isomerization Performance of MoOx-Pd/Ce-MCM-48 Catalyst.

Preparation of Pd/Ce(F)-MCM-48 catalysts and their catalytic performance of <i>n</i>-heptane isomerization

Preparation of Pd/Ce(F)-MCM-48 catalysts and their catalytic performance of n-heptane isomerization

Hydroisomerization of N-Heptane over HPMo-Ni/Ce-MCM-48 Catalysts

CO and Methane Oxidation Over CeXZr1-XO2 Mixed Oxide Supported PdO Catalysts

Catalytic Combustion of VOCs on Pt/CuMnCe and Pt/CeY Honeycomb Monolithic Catalysts

Synthesis of Mo-MCM-48 and Their Isomerization Performances of N -Heptane

N-Heptane Isomerization on MoOx Catalyst Supported by SiO2 As a Framework

Preparation and Catalytic Property of Moox with Meso-Porosity

Influences of Cerium on Structure and Catalytic Performance of N-Heptane Hydroisomerization of Ni-HPW/MCM-48

A Promising Moox-Based Catalyst for N-Heptane Isomerization

n-Heptane isomerization over mesoporous MoOx and Ni-MoO x catalysts

Nanocomposite Catalysts of Non-Purified MoVNbTeOx with CeO2 or TiO2 for Oxidative Dehydrogenation of Ethane

Synthesis of Cerium-Doped MCM-48 Molecular Sieves and Its Catalytic Performance for Selective Oxidation of Cyclohexane

Effects of Cerium Doping on Pt–Sn/Al2O3 Catalysts for N-Heptane Reforming

Elucidation of the Active Phase in Pd‐Based Catalysts Supporting on Octahedral CeO2 for Low‐Temperature Methane Oxidation

Enhancement of Methanol Oxidation Performance Over Pd/CeO2 Derived from MOF and Mechanism Investigation via In Situ Studies

Isomerization of o-Xylene Over Zeolite-Containing NiMoP/Al2O3Catalysts

A comparative study of catalytic partial oxidation of methane over CeO2 supported metallic catalysts

Catalytic performance of metal-organic framework (MOF) and micro-mesoporous composites as the supports for Pt catalysts for n-heptane isomerization

Catalytic Performance of Phase-Pure M1 MoVNbTeOx/CeO2 Composite for Oxidative Dehydrogenation of Ethane