n-Heptane isomerization over mesoporous MoOx and Ni-MoO x catalysts

Xinping Wang,Can Li,YingJun Wang,Tian-Xi Cai

DOI: https://doi.org/10.1016/j.cattod.2004.06.033

IF: 5.3

2004-01-01

Catalysis Today

Abstract:MoOx and Ni–MoOx catalysts with maximum pore diameter at ca. 4.1nm in the meso-pore range were prepared by reducing MoO3 or NiO doped MoO3 in H2 flow at 623K in a period of 6–12h. The catalysts were used in n-heptane isomerization isothermally carried out at 573K under atmospheric pressure in a conventional fixed-bed flow reactor. MoOx is predominantly composed of the MoOxHy and MoO2 phase. The former can be considered to be more active than the latter. Over the MoOx catalyst, the H2 partial pressure positively affected the reaction rate with an order of ca. 0.35. It can be deduced from the result that the MoOx catalyst lacks active sites with a metallic character for dehydrogenation–hydrogenation step in n-heptane isomerization. The Ni–MoOx catalysts have a lower specific surface area than the MoOx catalysts, due to that the reduction of MoO3 was accelerated by nickel, and the fact that more H2O was produced in the initial reduction process, this leading to MoOx sintering. Comparing with MoOx catalysts, the 5% Ni–MoOx catalysts are more active in terms of the reaction rate per unit surface area of the catalyst, the explanation is that the dehydrogenation–hydrogenation step in n-heptane isomerization is effectively enhanced by incorporation of Ni in the catalysts.