Abstract:The nanoindentation hardnesses of a commercially available soda-lime glass, a tetragonal ZrO2 polycrystalline and a hot-pressed Si3N4 were measured in the peak load range from 7.5 to 500 mN. The experimental results revealed that, for each material, the measured hardness exhibits a peak-load- dependence, i.e., indentation size effect (ISE). Such a peak-load-dependence was then analyzed using the Meyer’ law, the Hay–Kendall approach, the proportional specimen resistance (PSR) model, the elastic recovery model and the modified PSR model. The analyses revealed that: (1) Meyer's law provides a satisfactory description for the experimental data for each material but cannot provide any knowledge of the origin of the observed ISE; (2) the Hays–Kendall approach, the elastic recovery model and the PSR model yield meaningless values of the parameters included in the corresponding equations, invalidating the applicability of these models in analyzing the ISE in the nanoindentation region; (3) the modified PSR model is sufficient for describing the observed ISE but the physical meaning of this model seems to be more complex than those proposed originally. For each material, the true hardness was also determined based on the PSR model, the elastic recovery model and the modified PSR model, respectively. It was found that the true hardness values deduced based on different models are similar with each other and this similarity was attributed to the similarity between the empirical equations adopted in these models.

Determination of the Load-Independent Hardness by Analyzing the Peak-Load-Dependence of the Unloading Slope in Nanoindentation

Effect of peak load on the determination of hardness and Young's modulus of hot-pressed Si3N4 by nanoindentation

On the description of indentation size effect in hardness testing for ceramics: Analysis of the nanoindentation data

Description of the Nanoindentation Unloading Curves with a Universal Function: Theoretical Consideration and Applications to Brittle Materials

Effect of Load-Dependence of Hardness on Indentation Toughness Determination for Soda-Lime Glass

Analysis of the Nanoindentation Data Measured with a Berkovich Indenter for Brittle Materials: Effect of the Residual Contact Stress

A Universal Function for the Description of Nanoindentation Unloading Data: Case Study on Soda-Lime Glass

Prediction of Nanoindentation Hardness Profile from a Load-Displacement Curve

An Improved Work-Of-Indentation Approach For The Determination Of Hardness From Nanoindentation Tests

Description of Unloading Behavior of Berkovich Nanoindentation

On the Contact Area for Nanoindentation Tests with Berkovich Indenter: Case Study on Soda-Lime Glass

Indentation Size Effect in the Nanohardness of Soda-Lime Glass

Berkovich Nanoindentation of Zr55Cu30Al10Ni5 Bulk Metallic Glass at a Constant Loading Rate

On the Determination of Reduced Young's Modulus and Hardness of Elastoplastic Materials Using a Single Sharp Indenter

Nanoindentation Characterization of the Hardness of Zirconia Dental Ceramics

Analysis of Load-Displacement Curves of Ceramics Measured with Low-Load Vickers Hardness Test: Indentation Size Effect

Influence of Friction in Material Characterization in Microindentation Measurement.

Testing effects on hardness of a Zr-based metallic glass under nanoindentation

An energy-balance analysis for the size effect in low-load hardness testing

Load dependence of the apparent hardness of silicon nitride in a wide range of loads

Comparison of nano-indentation hardness to microhardness