Abstract:In this work, the effects of Nb2O5 addition on the dielectric properties and phase formation of BaTiO3 were investigated. A core–shell structure was formed for Nb-doped BaTiO3 resulted from a low diffusivity of Nb5+ ions into BaTiO3 when grain growth was inhibited. In the case of 0.3–4.8 mol% Nb2O5 additions, two dielectric constant peaks were observed. The Curie dielectric peak was determined by the ferroelectric-paraelectric transition of grain core, whereas the secondary broad peak at lower temperature was due to strong chemical inhomogeneity in Nb-doped BaTiO3 ceramics. The dielectric constant peak at Curie temperature was markedly depressed with the addition of Nb2O5. On the other hand, the secondary dielectric constant peak was enhanced when sintered above 1280 °C for higher Nb2O5 concentrations (≥1.2 mol%). The Curie temperature was shifted to higher temperatures, whereas the transition temperature corresponding to the secondary peak moved to lower temperatures as increasing the amount of Nb2O5 more than 1.2 mol%. The decrease of this lower transition temperature was assumed to be closely related with the secondary phase formation when Nb concentration greater than 1.2 mol%. From XRD analyses, a large amount of secondary phases was observed when Nb2O5 amount exceeded 1.2 mol%. The coefficients of thermal expansion of Nb-doped BaTiO3 were increased with increasing Nb2O5 contents, resulting in large internal stress between cores and shells. Therefore, the shift of Curie temperature to higher temperatures was attributed to internal stress resulting from the formation of a core–shell structure and a large amount of secondary phase grains.

Effect of Co<inf>2</inf>O<inf>3</inf>-doped on Dielectric Properties of Tungsten-Bronze Structure Ceramic Ba<inf>4</inf>Eu<inf>2</inf>Fe<inf>2</inf>Nb<inf>8</inf>O<inf>3</inf>0<inf>30</inf>

Effect of Co2O3-doped on dielectric properties of tungsten-bronze structure ceramic Ba4Eu2Fe2Nb8O3030

Colossal Dielectric Permittivity in (al+nb) Co-Doped Ba0.4Sr0.6TiO3 Ceramics

Dielectric ceramics with tungsten-bronze structure in the BaO-Nd<sub>2</sub>O<sub>3</sub>-TiO<sub>2</sub>-Nb<sub>2</sub>O<sub>5</sub> system

Dielectric, Optical, and Multiferroic Properties of Co-doped SrBi2Nb1.8Fe0.2O9 Ceramics

Eu-substitution-induced Commensurate Phase with Enhanced Ferroelectric Property in Ba-4(EuxLa1-x)(2)Fe2Nb8O30 Multiferroics

Dielectric Ceramics with Tungsten-bronze Structure in the BaO–Nd 2 O 3 –TiO 2 –Nb 2 O 5 System

Oxygen-vacancy-induced Reversible Control of Ferroelectric Polarization in Ba4Eu2Fe2Nb8O30 Ceramics

Dielectric and Ferroelectric Properties of Ba4Gd2Fe2Nb8O30 with Filled Tungsten-Bronze Structure

Ferroelectric Phase Transition and Low-Temperature Structure Fluctuations in Ba4Nd2Ti4Nb6O30 Tungsten Bronze Ceramics

Robust and tunable ferroelectricity in Ba/Co co-doped (K 0.5 Na 0.5 )NbO 3 ceramics

The effect of co-substitution on the microwave dielectric properties of Ba6-3Nd8+2Ti18O54(x=2/3) ceramics

Effects of W,Ti Co-Doping on the Microstructure and Microwave Dielectric Properties of Ba5nb4o15 Ceramics

Dielectric behaviors of Nb2O5–Co2O3 doped BaTiO3–Bi(Mg1/2Ti1/2)O3 ceramics

Effects of Ta2o5/Y2o3 Codoping on the Microstructure and Microwave Dielectric Properties of Ba(Co0.56zn0.40)(1/3)Nb2/3o3 Ceramics

Robust and Tunable Ferroelectricity in Ba/Co Co-Doped (k0.5na0.5)nbo3 Ceramics

Effects of Nb 2 O 5 Doping on the Microstructure and the Dielectric Temperature Characteristics of Barium Titanate Ceramics

Dielectric and Ferroelectric Characteristics of Ba5NdFe1.5Nb8.5O30 Tungsten Bronze Ceramics

Tuning Ferroelectric, Dielectric, and Magnetic Properties of BiFeO3 Ceramics by Ca and Pb Co‐Doping

Dielectric Properties and High-Temperature Dielectric Relaxation of Tungsten-Bronze Structure Ceramics Ba2gdfenbta3o15

Crystal structure and dielectric properties of ferroelectric ceramics in the BaO-Sm2O3-TiO2-Nb2O5 system

Effect of Co&lt;inf&gt;2&lt;/inf&gt;O&lt;inf&gt;3&lt;/inf&gt;-doped on Dielectric Properties of Tungsten-Bronze Structure Ceramic Ba&lt;inf&gt;4&lt;/inf&gt;Eu&lt;inf&gt;2&lt;/inf&gt;Fe&lt;inf&gt;2&lt;/inf&gt;Nb&lt;inf&gt;8&lt;/inf&gt;O&lt;inf&gt;3&lt;/inf&gt;0&lt;inf&gt;30&lt;/inf&gt;