Abstract:In this study, both polyvinyl chloride (PVC) and polyacrylonitrile (PAN) were dissolved in dimethyl formaldehyde (DMF) with 8 wt. % concentrations at 25 : 75, 50 : 50, and 75 : 25 of PVC: PAN blending. For the investigation of the homogeneity and compatibility of mixture polymer solutions, it is examined by rheological properties such as viscosity, shear stress, shear rate, and calculation of the flow behavior index, while the investigation of the stability and high density of nanofibers without beads used field-emission scanning electron microscopy (FE-SEM), Fourier transform near-infrared spectroscopy (FT-NIR), X-ray diffraction (XRD), and differential scanning calorimetry-thermogravimetric analysis (DSC-TGA). The results show that blending of PAN with PVC leads to improving of the electro spun ability of PVC with more stability, and the mean nanofiber diameter was 90.873 ± 40.82 nm at 25 : 75 PVC: PAN. Moreover, mechanical properties are ultimate tensile strength and modulus of elasticity decreasing with decreasing the blending ration from pure PVC to 75 : 25 PVC: PAN nanofibers by 71% and 83%, respectively, while the elongation at break increases by 79%, and decomposition temperatures decreased from 451.96 to 345.38°C when changing the PVC content from pure PVC to 25 : 75 PVC: PAN. On the other hand, changing of the nanofiber behavior from hydrophobicity to hydrophilic increased the PAN content in PVC: PAN blends. Furthermore, the low interaction between the chains of polymers and the crystallinity (%) and crystalline size (nm) of blend nanofibers slightly decreased compared to the pure polymers. According to all tests, the 25: 75 PVC: PAN was the best blending ratio, which gave a more stable nanofiber produced at low concentrations and more compatible between the PVC and PAN.

Study on BC/PAN Blending Nanofibers by Elecrtospinning

Characterization Of Pan/Pani-Dbsa Blend Nanofibers Produced By Electrospinning Method

Preparation of Polyacrylonitrile and Polystyrene Blend Fibers Through Electrospinning

Improving the Physical Properties of Nanofibers Prepared by Electrospinning from Polyvinyl Chloride and Polyacrylonitrile at Low Concentrations

Modification of polyacrylonitrile nanofibers by blending with polyurethane

Preparation of porous polyacrylonitrile fibers by electrospinning a ternary system of PAN/DMF/H2O

PREPARATION OF POROUS POLYACRYLONITRILE ULTRATHIN FIBERS BY ELECTROSPINNING WITH NONSOLVENT INDUCED PHASE SEPARATION

The effects of electrospinning parameters on coaxial polyacrylonitrile/polyurethane nanofibers: Morphology and water vapour transmission rate

Enhancement of mechanical and physical properties of electrospun PAN nanofiber membranes using PVDF particles

Fabrication and Characterization of Electrospun Poly(acrylonitrile- co-Methyl Acrylate)/Lignin Nanofibers: Effects of Lignin Type and Total Polymer Concentration

Preparation of porous hollow polyacrylonitrile ultrafine fibers by coaxial electrospinning

Enhanced Mechanical Performance of Electrospun Graphene/Polyacrylonitrile (PAN) Composite Microfibrous Yarns Via Post-Processing

Study on electrospinnability of PVP/PEO composite micro-nano fibers

SYNTHESIS AND CHARACTERISTICS OF POLYACRYLONITRILE (PAN) NANOFIBER MEMBRANE USING ELECTROSPINNING METHOD

Structure and Morphological Evolvement of Electrospun Polyacrylonitrile/Organic–Modified Fe-Montmorillonite Composite Carbon Nanofibers

Advancing Nanofiber Research: Assessing Nonsolvent Contributions to Structure Using Coaxial Electrospinning

Study on the Mass Transfer Process in Pan Wet-Spinning

Electrically Conductive PANI-DBSA/Co-PAN Composite Fibers Prepared by Wet Spinning

Preparation and Properties of Poly (vinyl Alcohol) Nanofibers by Electrospinning

Wet-Spun Side-by-Side Electrically Conductive Composite Fibers

Preparation of PAN@PU coaxial electrostatic spun nanofibers for oil/water separation