Characterizations and Catalytic Properties of Transition Metal Ions Incorporated in Mesoporous Materials

Yuanyuan Wang,Jian‐Liang Ye

2004-01-01

Abstract:Mesoporous materials typified by MCM-41 possess well-ordered mesoporous channels with controllable pore sizes from 2-30 nm, and are expected as desirable materials for catalysis.However, silicious mesoporous materials generally do not have sufficient intrinsic catalytic activities.Thus many studies have focused on introducing catalytically active sites. It is expected that different synthetic methods would result in different coordination structures of metal cations introduced in MCM-41, and thus different catalytic properties in catalytic reactions. The author's group has used two methods, i.e., direct hydrothermal synthesis (DHT) and template-ion exchange (TIE), for the syntheses of V-, Fe-, and Cr-MCM-41 and applied them as catalysts to selective oxidations of hydrocarbons. This paper highlights the characterizations of the coordination structures of these metal cations introduced into MCM-41 by the DHT and the TIE methods, and the structural-property relationships of these metal ion-containing MCM-41 materials in selective oxidation reactions.MCM-41 was prepared by hydrothermal synthesis using hexadecyltrimethylammonium bromide and sodium silicate as the sources of template and silicon, respectively. In the DHT method, metal cations were directly added into the synthesis gel before hydrothermal synthesis, while the exchanging of metal ions in ethanolic solutions with the template cations contained in the uncalcined MCM-41 was performed in the TIE method. XRD and N2-adsorption measurements showed that the mesoporous regularity was not destroyed with both synthetic methods for all the metal ion-containing MCM-41 with appropriate contents of metal cations.For V-MCM-41, the characterizations with mainly EXAFS suggested that V5+ cations were in tetrahedral coordination and mainly incorporated inside the framework of MCM-41 to substitute Si4+in the samples by the DHT method. Tetrahedrally coordinated Vanadyl species were also obtained by the TIE method, but the VO4 was dispersed on the wall surface of MCM-41. The V