Abstract:We report here a generalized synthesis of various crystalline mesoporous metal oxides including CeO2, Cr2O3, Fe2O3, SnO2, Ce0.5Zr0.5O2, TiO2, Al2O3 and ZrO2 from the self-assembly of a basic poly 4-vinylpyridine (P4VP) template with various metal precursors based on their strong acid–base interaction under high temperature (180 °C) hydrothermal conditions. Using the typically crystalline mesoporous metal oxide of CeO2, after removing the template by calcination at 550 °C and loading with various transition metal oxides such as MnOx, various transition metal oxide functionalized crystalline mesoporous CeO2 (MnOx/P4VP–CeO2) were obtained. X-ray diffraction (XRD) patterns show that the resulting mesoporous metal oxides exhibit a high degree of crystallinity, and the transition metal oxides active sites have been successfully loaded into these samples. N2 sorption–desorption isotherms, SEM images show that the resulting crystalline mesoporous metal oxides, such as CeO2, have a large BET surface area (94 m2 g−1) and abundant mesopores, which exhibit monolithic morphology with crystal sizes ranging from 5 to 15 μm, giving a uniform pore size centered at 5 nm. XPS spectra show that the active sites such as MnOx exhibit the phases of MnO2 and Mn2O3 in P4VP–CeO2. H2-TPR curves show that MnOx/P4VP–CeO2 exhibits decreased reductive temperatures of both active sites of the MnOx and P4VP–CeO2 supporter when compared with the samples reported previously. More importantly, MnOx/P4VP–CeO2 exhibits much better catalytic activities and good recyclability for catalyzing the oxidation of benzene than that of MnOx loaded commercially crystalline CeO2, which will be very important for their wide applications for VOCs removal in industry.

Crystalline Mesoporous Transition Metal Oxides: Hard-Templating Synthesis and Application in Environmental Catalysis

Low-Temperature Synthesis of Tunable Mesoporous Crystalline Transition Metal Oxides and Applications as Au Catalyst Supports

Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides

Metal and Metal Oxide Supported on Ordered Mesoporous Carbon as Heterogeneous Catalysts

Ordered Crystalline Mesoporous Oxides As Catalysts for CO Oxidation

Generalized and High Temperature Synthesis of a Series of Crystalline Mesoporous Metal Oxides Based Nanocomposites with Enhanced Catalytic Activities for Benzene Combustion

Ordered Mesoporous Materials with Improved Stability and Catalytic Activity

Mesoporous Carbon Materials: Synthesis and Modification.

Catalytic Decomposition of N<SUB>2</SUB>O on Ordered Crystalline Metal Oxides

Research Progress in Synthesis of Crystalline Mesoporous Transition Metal Oxides

Heterogeneous Catalysis in Zeolites, Mesoporous Silica, and Metal–Organic Frameworks

Mesoporous metal oxide via nanocasting: Recent advances on types of templates, properties, and catalytic activities

Mesoporous Zeolites and Their Catalytic Performance

Designing and Fabricating Ordered Mesoporous Metal Oxides for CO2 Catalytic Conversion: A Review and Prospect

Hydrothermally Stable and Catalytically Active Ordered Mesoporous Materials Assembled from Preformed Zeolite Nanoclusters

Template Synthesis of Porous Ceria-Based Catalysts for Environmental Application

Preparation and Application of Ordered Mesoporous Metal Oxide Catalytic Materials

Catalysis in Single Crystalline Materials: from Discrete Molecules to Metal-Organic Frameworks

Ordered macroporous MOF-based materials for catalysis

Catalytic Removal of Volatile Organic Compounds over Porous Catalysts

Metal–organic Framework-Derived Porous Materials for Catalysis