Abstract:Carbon free composites Li1−xMgxFePO4 (x=0.00, 0.02) were synthesized from LiOH, H3PO4, FeSO4 and MgSO4 through hydrothermal route at 180°C for 6h followed by being fired at 750°C for 6h. The samples were characterized by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), flame atomic absorption spectroscopy and electronic conductivity measurement. To investigate their electrochemical properties, the samples were mixed with glucose as carbon precursors, and fired at 750°C for 6h. The charge–discharge curves and cycle life test were carried out at 23±2°C. The Rietveid refinement results of lattice parameters of the samples indicate that the magnesium ion has been successfully doped into the M1 (Li) site of the phospho-olivine structure. With the same order of magnitude, there is no material difference in terms of the electronic conductivities between the doped and undoped composites. Conductivities of the doped and undoped samples are 10−10Scm−1 before being fired, 10−9Scm−1 after being fired at 750°C, and 10−1Scm−1 after coated with carbon, respectively. Both the doped and undoped composites coated with carbon exhibit comparable specific capacities of 146mAhg−1 vs. 144mAhg−1 at 0.2C, 140mAhg−1 vs. 138mAhg−1 at 1C, and 124mAhg−1 vs. 123mAhg−1 at 5C, respectively. The capacity retention rates of both doped and undoped samples over 50 cycles at 5C are close to 100% (vs. the first-cycle corresponding C-rate capacity). Magnesium doping has little effects on electronic conductivity and electrochemical properties of LiFePO4 composites prepared via hydrothermal route.

Research on Transport of Charge Carriers in LiFe_(1-x)Mg_xPO_4/C

Influence Mechanism of Mg 2+ Doping on Electrochemical Properties of LiFePO 4 Cathode Materials

Electrochemical behavior of Mg-doped 7LiFePO 4 –Li 3 V 2 (PO 4 ) 3 composite cathode material for lithium-ion batteries

Studies on Electrochemical Behavior of Mg-doped LiFePO4

Structure and Electrochemical Performance of Mg~(2+) Doped LiFePO_4/C

Mg-doped Porous Spherical LiFePO4/C with High Tap-Density and Enhanced Electrochemical Performance

Improving the Electrochemical Performance of Lifepo4/C by Doping Magnesium Trisilicate

Synthesis and electrochemical performance of Li1-xLaxFe1-yMgyPO4/C cathode

Influence of Mg Ion Doping on the Battery Properties of Lifepo4/C

Influence of Surface Modification and Mg Ion Doping on Structure and Properties of LiFePO4

Mg-doped LiMnPO4/C Cathode Materials for Enhanced Lithium Storage Performance

Effects of Carbon Coating and Metal Ions Doping on Low Temperature Electrochemical Properties of LiFePO4 Cathode Material

B-Mg Co-Doping Behavior of LiFePO4 Cathode Material: Balance of Oxygen Vacancy and Enhancement of Electrochemical Performance

Hierarchical LiFe0.98MII 0.02PO4/C (MII = Ni, Mn, Mg) Composites Via Co-Doping for Lithium Ion Batteries

The prepared and electrochemical property of Mg-doped LiMn0.6Fe0.4PO4/C as cathode materials for lithium-ion batteries

Effect of Mg2+ Doping on Structure and Electrochemical Performance of Lithium Magnesium Silicate

Effects of Magnesium Doping on Electronic Conductivity and Electrochemical Properties of Lifepo4 Prepared Via Hydrothermal Route

Effect of Mn content on electrochemical performance and energy density of LiFe1-xMnxPO4/C

Effects of Neodymium Aliovalent Substitution on the Structure and Electrochemical Performance of LiFePO4

Effect of F-doping on the properties of LiFePO4-x/3Fx/C cathode materials via wet mechanical agitation-assisted high-temperature ball milling method

Doping Effects on Electronic Conductivity and Electrochemical Performance of Lifepo4