Abstract:Carbon free composites Li1−xMgxFePO4 (x=0.00, 0.02) were synthesized from LiOH, H3PO4, FeSO4 and MgSO4 through hydrothermal route at 180°C for 6h followed by being fired at 750°C for 6h. The samples were characterized by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), flame atomic absorption spectroscopy and electronic conductivity measurement. To investigate their electrochemical properties, the samples were mixed with glucose as carbon precursors, and fired at 750°C for 6h. The charge–discharge curves and cycle life test were carried out at 23±2°C. The Rietveid refinement results of lattice parameters of the samples indicate that the magnesium ion has been successfully doped into the M1 (Li) site of the phospho-olivine structure. With the same order of magnitude, there is no material difference in terms of the electronic conductivities between the doped and undoped composites. Conductivities of the doped and undoped samples are 10−10Scm−1 before being fired, 10−9Scm−1 after being fired at 750°C, and 10−1Scm−1 after coated with carbon, respectively. Both the doped and undoped composites coated with carbon exhibit comparable specific capacities of 146mAhg−1 vs. 144mAhg−1 at 0.2C, 140mAhg−1 vs. 138mAhg−1 at 1C, and 124mAhg−1 vs. 123mAhg−1 at 5C, respectively. The capacity retention rates of both doped and undoped samples over 50 cycles at 5C are close to 100% (vs. the first-cycle corresponding C-rate capacity). Magnesium doping has little effects on electronic conductivity and electrochemical properties of LiFePO4 composites prepared via hydrothermal route.

Effects of Carbon Coating and Metal Ions Doping on Low Temperature Electrochemical Properties of LiFePO4 Cathode Material

Improved Electrochemical Performance And Capacity Fading Mechanism Of Nano-Sized Limn0.9fe0.1po4 Cathode Modified By Polyacene Coating

Effect of Heteroatom Doping on Electrochemical Properties of Olivine LiFePO4 Cathodes for High-Performance Lithium-Ion Batteries

One-Step Solid-State Synthesis And High-Temperature Electrochemical Performance Of Carbon Coated Lifepo4 Cathode

Optimization of Carbon Coatings on LiFePO4: Carbonization Temperature and Carbon Content

Effect of CeO2-coating on the electrochemical performances of LiFePO4/C cathode material

Effect of Carbon Coating on Low Temperature Electrochemical Performance of Lifepo4/C by Using Polystyrene Sphere As Carbon Source

Doping Effects on Electronic Conductivity and Electrochemical Performance of Lifepo4

Effects of carbon coating and iron phosphides on the electrochemical properties of LiFePO4/C

Boron and Phosphorus Dual-Doped Carbon Coating Improves Electrochemical Performances of LiFe 0.8 Mn 0.2 PO 4 Cathode Materials

Improving the Rate and Low-Temperature Performance of LiFePO 4 by Tailoring the Form of Carbon Coating from Amorphous to Graphene-Like

Effect of carbon coating on the electrochemical performance of LiFePO4/C as cathode materials for aqueous electrolyte lithium-ion battery

Enhance electrochemical performance of LiFePO4 cathode material by Al-doped Li7La3Zr2O12 and carbon co-coating surface modification

Improving the rate and low-temperature performance of LiFePO4 by tailoring the form of carbon coating from amorphous to graphene-like

Preparation and Electrochemical Properties of Carbon-Coated LiMn0.6Fe0.4PO4 Cathode Material for Lithium-Ion Batteries

Electrochemical Performance and Kinetics of LiFePO4/C Cathode in a Low-Temperature Electrolyte

Effects of Magnesium Doping on Electronic Conductivity and Electrochemical Properties of Lifepo4 Prepared Via Hydrothermal Route

Enhanced Electrochemical Property of FePO4-coated LiNi0.5Mn1.5O4 As Cathode Materials for Li-ion Battery

The Influence of Porous Structure on the Electrochemical Properties of LiFe0.5Mn0.5PO4 Cathode Material Prepared by Mechanochemically Assisted Solid-State Synthesis

Effect of F-doping on the properties of LiFePO4-x/3Fx/C cathode materials via wet mechanical agitation-assisted high-temperature ball milling method

Effect of Ti doping on LiFePO4/C cathode material with enhanced low-temperature electrochemical performance