Effect of Y_2O_3 Content on Microstructure and Properties of Molybdenum Alloys

Jianming Ruan

2012-01-01

Abstract:The effects of Y2O3 content on microstructure and mechanical properties of molybdenum alloys were studied.Mo-Y alloys with different Y2O3 contents were prepared by powder metallurgy(P/M) method.Mo-Y alloys fracture characteristic and microstructure were characterized by metallographic microscope,SEM,XRD and EDS,respectively.The results show that the performances of the alloys improved by adding Y2O3 due to the grain size can be refined and become uniform and the density of alloy can be improved through adding Y2O3.With increasing Y2O3 content,tensile strength and yield strength of alloys increase firstly and then decrease.When Y2O3 content is 1%,tensile strength and yield strength are 511.43 MPa and 456.99 MPa,which are 1.31 times and 1.57 times of pure Mo alloy,respectively,and the optimum mechanical poperties of Mo-Y alloys are obtained.The Y2O3 particles with sphericity and isometric shape distribute homogeneoully on the molybdenum grain boundaries of the sintered alloys.