Microstructure Evolution Mechanism and Mechanical Properties of Laser Solid Formed Ti-6Al-xMo Alloys Based on Different Mo Additions
Zhang Fengying,Yang Sen,Huang Kaihu,Chen Xi,Chen Yongnan,Mei Min,Wang Meng,Tan Hua
2022-01-01
Rare Metal Materials and Engineering
Abstract:Based on Mo equivalent design, novel Ti-6Al-xMo (x=2, 3, 4) titanium alloys were deposited by laser solid forming ( LSF) from mixed Ti, Al and Mo elemental powders, and the microstructure and tensile properties of the alloys were investigated at room temperature. The results show that the solidification microstructure of the three alloys presents coarse columnar grains growing along the direction of < 100 >, and the top is composed of equiaxed grains. With the increase of Mo content, the average width of the columnar grains decreases, and the thickness of the equiaxed grains layer increases gradually. The microstructure in primary ss grains is composed of primary alpha lath and retained ss phase, and there also exists grain boundary alpha and alpha colonies. With the increase of Mo content, the width and area ratio of primary alpha lath decrease. When the Mo content increases to 4wt%, the secondary alpha phase appears in the grain. Moreover, 12 kinds of alpha variants are found in all the three components by EBSD analysis, and the variation is dominant. In terms of mechanical properties, the strength and hardness increase with the increase of Mo content while the elongation decreases. By contrast, Ti-6Al-2Mo and Ti-6Al-3Mo have the very good tensile properties with tensile strength of 962 MPa and elongation of 11.5%, and tensile strength of 982 MPa and elongation of 9.2%, respectively.