Influence of Y2O3 on Sintering Performance and Micro-Structure of Ultrafine Mo Composite Powders

CHENG Hui-chao,LIU Pin-pin,FAN Jing-lian,TIAN Jia-min,LI Peng-fei

DOI: https://doi.org/10.3969/j.issn.1673-0224.2011.03.007

2011-01-01

Abstract:Ultrafine composite powders(Mo+Y) was synthesized by sol-spray drying,calcination and hydrogen reduction processes using ammonium paramolybdate((NH4)6Mo7O24?4H2O) and yttrium nitrate(Y(NO3)3?6H2O) as raw materials.The powders were subjected to a series of processes including press forming,pre-sintering and high-temperature sintering,then fine-grained Mo alloy was obtained.The influences of rare-earth Y on the sintering performance of the Mo powders as well as the micro-structure of the sintered Mo material were studied.Results show that,Y exists in ultrafine Mo powders as the form of Y2O3 after hydrogen reduction,and it refines the grain size of Mo powders.In addition,Y enhances the sintering activity of ultrafine Mo powders,suppresses the grain growth of Mo during sintering.However,the grain size reduction of the Mo powders leads to an increase of oxygen content,which has a negative effect on the alloy density.When the adding amount of Y is too little,the grain size of Mo is large,the density is low and the increase of strength is unobvious;on the other hand,an more addition of Y would lead to the excessive distribution of Y2O3 in Mo grainboundaries,which would result in an obvious decrease in alloy plasticity.When the mass fraction of Y is 2%,the alloy has a preferable combination properties,with the grain size of 3～5 μm and the tensile strength of 620 MPa.