Abstract:The currently used low carbon operation in blast furnaces (BFs) leads to a thin coke layer and deterioration in gas and liquid permeability. Previous studies have reported that coke breeze, formed by the graphitization of coke, is one of the main influences on gas and liquid permeability in the high-temperature zone of a BF. To investigate the influence of the graphitization of BF coke on its metallurgical properties, the degree of coke graphitization under different heating temperatures from 1100 to 1500℃ was investigated. The dependence of the degree of graphitization on coke reactivity index (CRI) and coke strength after reaction (CSR) was also studied. The relationship between different degrees of graphitization in coke and alkali metals was clarified. Finally, the micro-morphology of coke was inspected and analyzed. Results show that with increasing temperature, the degree of coke graphitization intensifies. With every 100℃ rise in heating temperature, the degree of coke graphitization increases 1.8 times, the value of the spacing of layers (d002) decreases by 2%, and the values of the layers diameter of microcrystalline structure (La) and the stack height (Lc) are improved by 3% and 15%, respectively. In addition, it is observed that the surface stomata of the coke decreases particularly the large pores, the mosaic structure decreases, the isotropic structure increases, and the degree of structural ordering increases. When the degree of graphitization intensifies, the CRI of the coke gradually decreases, the CSR gradually increases, the degree of coke degradation weakens, the formed large pores reduced, and the trend for pore wall damage is reduced. Moreover, the alkali metal plays a catalytic role in improving the CRI and decreasing the CSR. It is considered that the graphitized coke resists the destruction of the alkali metal and thus decreases the degree of coke degradation.

Reactivity and Post-reaction Properties of Coke and Their Measurement

Effect of Pore Structure and Matrix Reactivity on Coke Reactivity and Post-Reaction Strength

Effects of Microscopic Characteristics on Post-Reaction Strength of Coke

Effects of Solution Loss Degree, Reaction Temperature, and High Temperature Heating on the Thermal Properties of Metallurgical Cokes

Multi-factors Affecting Coke Solution Loss Reaction

Low CRI, High CSR Coke Trials

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

Highly Reactive Coke Made from Low-rank Coal: Relationship Between Thermal Properties and Multilevel Structure

Effect of Coarser Fraction on Coke Strength After Reaction (CSR) of Coke Plant Blend at Tata Steel

Degradation Behaviors of Coke under Complex Solution Loss Conditions

The effect of alkali on the reaction kinetics and strength of blast furnace coke

Kinetics and mechanisms of coke and sinter on the coupling reaction to evaluate the integrated effects of coke solution loss reaction on blast furnace processes

Influence of solution loss reaction temperature to the thermal properties of high reactivity coke

Application of High‐ and Low‐Reactivity Cokes in Hydrogen‐Rich Blast Furnaces

Metallurgical Coke Combustion with Different Reactivity under Nonisothermal Conditions: A Kinetic Study

Research on the Post-reaction Strength of Iron Coke Hot Briquette under Different Conditions

The solution-loss reaction of cokes with different reactivity and lump ores during reductive coupling

A comprehensive investigation on the structural transformation and dissolution loss reaction of coke during gasification in CO 2 atmosphere

A Comprehensive Review of Characterization Methods for Metallurgical Coke Structures

Effect of gasification reaction on pore structure, microstructure, and macroscopic properties of blast furnace coke

Characterization of Porosity Changes during Reaction of Coke and Coke Analogues with CO2 Using Micro‐Computer Tomography