Abstract:The pseudocapacitive materials, like spinel NiCo2O4 (NCO), that use Faradaic reactions to store charge have been widespread paid attention for supercapacitors application. So, it is a basic fundamental guideline that the preparation of higher-performance pseudocapacitive materials depends on achieving and accelerating more Faradaic reactions in the aspect of electrodes. In this work, based on the mentioned principle, we report a facile method that could significantly promote the capacity of NiCo2O4 nanoelectrode through annealing precursor nanowires (NWs) in different volume ratios of N-2 and O-2 condition. The pristine NCO (V-N2: V-O2 = 0: 1) only exhibited inferior performance with a specific capacitance of 0.88 F cm(-2) (338.5 F g(-1) at 2mA cm(-2)) and capacitive retention of 54% from 2 to 30mA cm(-2). While, for a comparison, the highest comprehensive performance of NCO-9 (V-N2: V-O2 = 9: 1) electrodes delivered superior specific capacitance of 3.8 F cm(-2) (1461 F g(-1) at 2mA cm(-2)), excellent rate retention of 77% and good cycling stability. These boosted pseudocapacitive properties both in capacity and rate capability are attributed to the severe oxygen vacancy defects introduced in nitrided NCO NWs. The involving richness-enabled oxygen defects significantly enhance the electron/ions transportation, and then efficiently alter the well-known capacitive surfacial reaction into bulk pattern in the charge-discharge cycles. This dramatically increased electron/ions kinetics and electrochemical cites for Faradaic reactions. These results provide a deep insight into correlating oxygen vacancies induced structural and chemical evolution on enhanced capacitive performances of redox-active-NiCo2O4 materials. (C) 2018 Elsevier Ltd. All rights reserved.

Electrochemical Capacitance of Nano-Sized Nickel Oxide Derived from a Gel-Combustion Process

Preparation and Electrochemical Capacitance Characteristics of Nano-Ni(OH)_2 with High Specific Capacitance

Pseudo-capacitance of Ultrafine Nickel Hydroxide Prepared by Sol-gel Method

Preparation of Porous Nano-nickel Oxide by Fast Precipitation and Its Capacitance Characteristics

Characterization of NiCo2 O4 as high-performance supercapacitor electrode materials

Efficient Utilization of Oxygen-Vacancies-enabled NiCo2O4 Electrode for High-Performance Asymmetric Supercapacitor

Electrochemical Behavior of Activated-Carbon Capacitor Material Loaded with Nickel Oxide

Electrochemical Capacitance of CoxNiyO Preparation by Microwave-assisted Modification

Preparation of NiMn2O4 with Large Specific Surface Area from an Epoxide-Driven Sol−gel Process and Its Capacitance

Synthesis and characterization of aerogel-like mesoporous nickel oxide for electrochemical supercapacitors

A Facile and Cost-Effective Synthesis of Mesoporous NiCo 2 O 4 Nanoparticles and Their Capacitive Behavior in Electrochemical Capacitors

Preparation and Electrochemical Properties of Nickel Oxide by Molten-Salt Synthesis

Electrochemical Fabrication of a Porous Nanostructured Nickel Hydroxide Film Electrode with Superior Pseudocapacitive Performance

Pseudocapacitive Behavior Of Nickel Oxide/Carbon Nanotubes Composite Prepared By Cathodic Deposition

Nickel Oxide Aerogel for High Performance Supercapacitor Electrodes

Spray pyrolyzed thorn-like nanostructured nickel oxide electrodes for symmetric supercapacitor device

Nanocrystalline LiNi1-xCoxO2 cathode materials prepared by a gel-combustion process

Comparative studies of nickel oxide films on different substrates for electrochemical supercapacitors

Controllable in Situ Synthesis of Ni(OH)2 and NiO Films on Nickel Foam As Additive-Free Electrodes for Electrochemical Capacitors

Electrochemical Capacitor with the Electrode of Nickel Hydroxide/Carbon Nanotube Composite