Abstract:The present work reports on a method of ultrasound emulsification-Pickering emulsion polymerization, which was developed to fabricate polystyrene (PSt) microspheres through the assistant technique of ultrasonic emulsification in a reaction system consisting of the immobilizer aminolyzed poly(divinylbenzene-alt-maleic anhydride) nanoparticles (PDVB-alt-MAH nanoparticles, PDMNPs), the initiator 2,2-azobisisobutyronitrile (AIBN), the medium deionized water and monomer styrene (St). The morphology and diameter were characterized through scanning electronic microscope (SEM) and laser particle sizer. The influences of emulsion stability, mechanical agitation speed and stabilizer usage on polymerization were investigated, respectively. It can be found that ultrasonic emulsification and mechanical agitation were necessary for the formation and stabilization of emulsion; meanwhile, the diameter of PSt microspheres could be controlled in the range of 200 nm to 90 nm with increasing amount of aminolyzed PDMNPs. Moreover, studies on the polymerization kinetics and the chemical structure of PSt microspheres were then conducted through gel permeation chromatography (GPC), Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectra (XPS). Based on the results, the highlights of this polymerization method are as follows : (1) high efficiency of stabilization of aminolyzed PDMNPs; (2) simple device of ultrasonic emulsification; (3) the surfactant-free polymer microspheres with narrow-distributed diameter. Furthermore, this polymerization method was then successfully used in polymerizations of other oil-soluble monomers, such as methyl methacrylate (MMA), glycidyl methacrylate (GMA) and alpha-methyl styrene (AMS). It therefore indicated that the present work not only developed a novel strategy for Pickering emulsion polymerization, but also broadened the field of industrial preparation of polymer microspheres.

Fabrication of Carboxylic Groups Functionalized Poly(styrene-co-maleic Anhydride) Microspheres Via Membrane Emulsification-Solvent Evaporation Method

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

Synthesis and Characterization of Amphiphilic Centipede-Like Copolymer PS-PS-PMAA

Preparation of monodisperse polystyrene microspheres with different functional groups using soap-free emulsion polymerization

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Preparation and Characterization of Affinity Polymer Basic Microspheres by Soap-Free Emulsion Polymerization

Preparation of Carboxyl‐Functionalized Polystyrene/Silica Composite Nanoparticles

Synthesis and Structure of Hydrophobically Modified Polysulfobetaine Methacrylate

High-yield preparation of polymeric micelles with carboxyl groups in the core

EFFECT OF SOLVENTS ON PREPARING SURFACE-MACROPOROUS POLYSTYRENE

Studies on Preparation, Characterization and Application of Porous Functionalized Glycidyl Methacrylate-Based Microspheres

Preparation of Thiol-Modified Hairy Polystyrene Microspheres

Fabrication of polymer microspheres using titania as a photocatalyst and pickering stabilizer.

Preparation of polystyrene/EVA/CaCO3 microspheres using a novel one-pot method via a phase inversion emulsion process

Preparation of Porous Polylactide Microspheres by Emulsion‐solvent Evaporation Based on Solution Induced Phase Separation

Precise Fabrication of Porous Microspheres by Iso-Density Emulsion Combined with Microfluidics

Control of Particle Size and Carboxyl Group Distribution in Soap‐free Emulsion Copolymerization of Methyl Methacrylate–ethyl Acrylate–acrylic Acid

Preparation of Poly (MMA-S-DVB) Microspheres by Suspension Polymerization Method

Studies on Ultrasound Emulsification-Pickering Emulsion Polymerization with Aminolyzed PDVB-alt-MAH Nanoparticles As Stabilizer

Preparation of Polystyrene/Polyacrylamide Core-Shell Microspheres via Microfluidizer-Assistant Emulsification Template Methods for Oil Recovery Enhancement

Preparation and characterization of polystyrene microspheres in the presence of β-cyclodextrin